炭素microspheres/マグネシウムヒドロキシド化合物難燃剤による難燃性ポリエチレンテレフタレート【JST・京大機械翻訳】

Flame-retarded polyethylene terephthalate with carbon microspheres/magnesium hydroxide compound flame retardant

著者 (17件)： Yang Yaru (Key Laboratory of Interface Science and Engineering in Advanced Materials, Taiyuan University of Technology, Ministry of Education, Taiyuan, 030024, China) ,  Yang Yaru (College of Textile Engineering, Taiyuan University of Technology, Yuci, 030600, China) ,  Yang Yaru (School of Material Science and Engineering, Taiyuan University of Technology, Taiyuan, 030024, China) ,  Niu Mei (Key Laboratory of Interface Science and Engineering in Advanced Materials, Taiyuan University of Technology, Ministry of Education, Taiyuan, 030024, China) ,  Niu Mei (College of Textile Engineering, Taiyuan University of Technology, Yuci, 030600, China) ,  Dai Jinming (Key Laboratory of Interface Science and Engineering in Advanced Materials, Taiyuan University of Technology, Ministry of Education, Taiyuan, 030024, China) ,  Dai Jinming (College of Textile Engineering, Taiyuan University of Technology, Yuci, 030600, China) ,  Dai Jinming (School of Material Science and Engineering, Taiyuan University of Technology, Taiyuan, 030024, China) ,  Bai Jie (Key Laboratory of Interface Science and Engineering in Advanced Materials, Taiyuan University of Technology, Ministry of Education, Taiyuan, 030024, China) ,  Bai Jie (College of Textile Engineering, Taiyuan University of Technology, Yuci, 030600, China) ,  Xue Baoxia (Key Laboratory of Interface Science and Engineering in Advanced Materials, Taiyuan University of Technology, Ministry of Education, Taiyuan, 030024, China) ,  Xue Baoxia (College of Textile Engineering, Taiyuan University of Technology, Yuci, 030600, China) ,  Xue Baoxia (School of Material Science and Engineering, Taiyuan University of Technology, Taiyuan, 030024, China) ,  Song Yinghao (Key Laboratory of Interface Science and Engineering in Advanced Materials, Taiyuan University of Technology, Ministry of Education, Taiyuan, 030024, China) ,  Song Yinghao (College of Textile Engineering, Taiyuan University of Technology, Yuci, 030600, China) ,  Peng Yun (Key Laboratory of Interface Science and Engineering in Advanced Materials, Taiyuan University of Technology, Ministry of Education, Taiyuan, 030024, China) ,  Peng Yun (College of Textile Engineering, Taiyuan University of Technology, Yuci, 030600, China)
資料名： Fire and Materials  (Fire and Materials)
巻： 42  号： 7  ページ： 794-804  発行年： 2018年 
JST資料番号： A0928A  ISSN： 0308-0501  CODEN： FMATDV  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 新しい化合物難燃剤(炭素microspheres/マグネシウムヒドロキシド,CMSs/MHと略記)を用いて,ポリエチレンテレフタレート(PET)の火災性能を改善した。LOI,UL94,及びコーン試験の結果は,CMSs/MH/PET複合材料が,CMSsのMHに対する質量比が5:5で,CMSs/MH含有量が1.0wt%のPETにおいて,最良の火災性能を得たことを示した。Py-CS-MS,TGA-DSC結果およびチャー残渣の形態は難燃性機構を明らかにした。CMSs/MHは,初期燃焼段階での活性化エネルギーを増加させることにより,PETの熱安定性を増加させた。燃焼の第2段階では,CMSs/MHはフリーラジカルの再結合の機会を増加させ,燃焼を遅くした。さらに,CMSs/MHは熱分解生成物の架橋を促進し,さらにチャー層の連続性を改善した。このように,CMSs/MH/PET複合材料の緻密で連続的なチャー層が生成した。このチャー層は熱放出速度を減少させ,チャー残渣の量を増加させた。Copyright 2018 Wiley Publishing Japan K.K. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 複合材料 ,  熱放射 ,  ラジカル ,  火災 ,  *ポリエチレンテレフタレート ,  活性化エネルギー ,  *難燃性 ,  再結合 ,  *難燃剤 ,  熱安定性 ,  水酸化マグネシウム ,  チャー ,  連続性
準シソーラス用語： 質量比 , 【Automatic Indexing@JST】

著者キーワード (5件)： 炭素ミクロスフェア ,  複合材料 ,  難燃剤 ,  水酸化マグネシウム ,  ポリエチレンテレフタレート

分類 (1件)： 火災  (RA02020B)

タイトルに関連する用語 (6件)： 炭素 ,  マグネシウム ,  ヒドロキシド ,  難燃剤 ,  難燃性 ,  ポリエチレンテレフタレート