相境界による(K,Na)NbO_3セラミックの温度安定性の改良【JST・京大機械翻訳】

Modifying Temperature Stability of (K,Na)NbO₃ Ceramics through Phase Boundary

著者 (6件)： Lv Xiang (Department of Materials Science, Sichuan University, 610064, Chengdu, P. R. China) ,  Wu Jiagang (Department of Materials Science, Sichuan University, 610064, Chengdu, P. R. China) ,  Xiao Dingquan (Department of Materials Science, Sichuan University, 610064, Chengdu, P. R. China) ,  Zhu Jianguo (Department of Materials Science, Sichuan University, 610064, Chengdu, P. R. China) ,  Zhang Junwei (King Abdullah University of Science and Technology (KAUST), Physical Science and Engineering Division (PSE), Thuwal, 23955-6900, Saudi Arabia) ,  Zhang Xi-xiang (King Abdullah University of Science and Technology (KAUST), Physical Science and Engineering Division (PSE), Thuwal, 23955-6900, Saudi Arabia)
資料名： Advanced Electronic Materials  (Advanced Electronic Materials)
巻： 4  号： 9  ページ： e1800205  発行年： 2018年 
JST資料番号： W2482A  ISSN： 2199-160X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： (0.9-x)(K_0.5Na_0.5)(Nb_0.965Sb_0.035)O_3-0.01SrZrO_3-x(Bi_0.5Na_0.5)ZrO_3セラミックを,歪に及ぼす相境界の影響を例示するための例として選択した。温度依存誘電率と収束ビーム電子回折パターンは,x=0.03~0.04のセラミックにおける菱面体晶,斜方晶,および正方晶相の多相共存を確認した。興味深いことに,x=0.03のセラミックスは歪において温度安定性を改善し,例えば180°Cでの単極歪の高い保持(≒95%)と20~180°Cでの24%の低い変化を示した。モードを提案して,歪を効果的に調整する方法を示し,ニオブ酸カリウム系セラミックにおけるその温度安定性を強化した。Copyright 2018 Wiley Publishing Japan K.K. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 斜方晶系 ,  ニオブ酸カリウム ,  誘電率 ,  多相 ,  温度依存性 ,  *セラミック ,  三方晶系 ,  正方晶系 ,  *相境界
準シソーラス用語： 回折パターン ,  *温度安定性 , 【Automatic Indexing@JST】

著者キーワード (4件)： (KNa)NbO3セラミック ,  物理的機構 ,  歪 ,  温度安定性

分類 (2件)： 圧電気,焦電気,エレクトレット  (BM05040M) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (4件)： 相境界 ,  Na ,  セラミック ,  温度安定性