Microstructure evolution and mechanical property of ZrC-SiC/Ti6Al4V joints brazed using Ti-15Cu-15Ni filler

著者 (5件)： Shi J.M. (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, China) ,  Zhang L.X. (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, China) ,  Pan X.Y. (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, China) ,  Tian X.Y. (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, China) ,  Feng J.C. (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, China)
資料名： Journal of the European Ceramic Society  (Journal of the European Ceramic Society)
巻： 38  号： 4  ページ： 1237-1245  発行年： 2018年 
JST資料番号： E0801B  ISSN： 0955-2219  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ZrC-SiCセラミックとTC4合金は自己Ti-15Cu-15Niフィラーを用いたろう付けすることに成功した。異なるろう付け温度で得られた継手のミクロ組織と機械的特性を調べた。結果は,Ti-15Cu-15NiとTC4からTiはZrC-SiCと反応してZrC-SiCセラミックに隣接したTiC相を形成することを示した。ロウ付けシームでは,Ti_2(Ni, Cu)金属間化合物帯(IMC帯),亜共晶帯と過共析ゾーンが形成された。ろう付温度,ろう材にTC4の溶解に大きく影響し,継手のミクロ組織を決定した。ろう付シーム中のα-Tiの形成は硬さとろう付継ぎ目の脆性,ろう付継手の性質に有利なを減少させた。継手を970°Cおよび亀裂ろう付継ぎ目近傍のZrC-SiC母材中で伝搬しでロウ付けされた場合,継手強度は43MPaの最大値に達した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 脆性 ,  共晶 ,  金属間化合物 ,  *炭化ケイ素 ,  ろう付継手 ,  ろう材 ,  目地 ,  セラミック ,  亀裂 ,  硬度 ,  *チタン ,  合金 ,  *ろう付
準シソーラス用語： 継手強度 ,  TC4 , 【Automatic Indexing@JST】

著者キーワード (4件)： ZrC-SiCセラミック ,  ろう付け温度 ,  界面反応 ,  Property

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  ろう付  (WC07050C)

タイトルに関連する用語 (8件)： Ti ,  フィラー ,  ろう付 ,  SiC ,  継手 ,  ミクロ組織 ,  発達 ,  機械的性質