後橋かけ液晶高分子/ポリウレタンブレンドフィルムの光誘起曲げ挙動【Powered by NICT】

Photo-Induced Bending Behavior of Post-Crosslinked Liquid Crystalline Polymer/Polyurethane Blend Films

著者 (5件)： Pang Xinlei (Department of Materials Science, Fudan University, 220 Handan Road, Shanghai, 200433, China) ,  Xu Bo (Department of Materials Science, Fudan University, 220 Handan Road, Shanghai, 200433, China) ,  Qing Xin (Department of Materials Science, Fudan University, 220 Handan Road, Shanghai, 200433, China) ,  Wei Jia (Department of Materials Science, Fudan University, 220 Handan Road, Shanghai, 200433, China) ,  Yu Yanlei (Department of Materials Science and State Key Laboratory of Molecular Engineering of Polymers, Fudan University, 220 Handan Road, Shanghai, 200433, China)
資料名： Macromolecular Rapid Communications  (Macromolecular Rapid Communications)
巻： 39  号： 1  ページ： ROMBUNNO.201700237  発行年： 2018年 
JST資料番号： D0314B  ISSN： 1022-1336  CODEN： MRCOE3  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 感光性成分と軟質ポリウレタン(PU)マトリックスとして架橋液晶高分子(CLCP)をもつ光応答性ブレンド膜を作製することに成功した。一軸延伸後,低濃度でも,アゾベンゼン含有CLCPは効果的にphotoinert PUマトリックスへの光応答を,CLCPの効果的な分散のおかげで全ブレンド膜の高速光誘起曲げ挙動をもたらした。特に,ブレンド膜は室温で非偏光UV光に露出したとき光誘起変形を示した。膜は熱処理後unbends,膜中にランダムに配向したメソゲンは機械的伸張,膜を与える可逆的変形挙動により再配列することができた。感光性混合膜は,低コストで良好な機械的性質と良好な加工性を有しており,それは新世代アクチュエータのための有望な候補である。Copyright 2018 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 機械的性質 ,  メソゲン ,  熱処理 ,  紫外線 ,  加工性 ,  延伸 ,  *ポリウレタン ,  偏光 ,  アクチュエータ ,  *高分子液晶
準シソーラス用語： 一軸延伸 ,  混合膜 ,  光応答 ,  光感受性 ,  *光誘起 , 【Automatic Indexing@JST】

著者キーワード (5件)： 橋かけ液晶性重合体 ,  光誘起曲げ挙動 ,  光応答性ブレンドフィルム ,  ポリウレタン ,  後架橋

分類 (2件)： その他の高分子の反応  (CG03040H) ,  高分子固体の物理的性質  (CG02024U)

タイトルに関連する用語 (5件)： 橋かけ ,  液晶高分子 ,  光誘起 ,  曲げ ,  挙動