Al_3Ti/ADC_12複合材料の微細構造と機械的性質に及ぼすSr改質の影響【JST・京大機械翻訳】

Effect of Sr Modification on Microstructures and Mechanical Properties of Al₃Ti/ADC₁₂ Composites

著者 (8件)： Qingjie Wu (Nanchang University, Nanchang 330031, China) ,  Qingjie Wu (Key Laboratory of Light Alloy Preparation & Processing in Nanchang City, Nanchang 330031, China) ,  Hong Yan (Nanchang University, Nanchang 330031, China) ,  Hong Yan (Key Laboratory of Light Alloy Preparation & Processing in Nanchang City, Nanchang 330031, China) ,  Yuan Liu (Nanchang University, Nanchang 330031, China) ,  Yuan Liu (Key Laboratory of Light Alloy Preparation & Processing in Nanchang City, Nanchang 330031, China) ,  Zhi Hu (Nanchang University, Nanchang 330031, China) ,  Zhi Hu (Key Laboratory of Light Alloy Preparation & Processing in Nanchang City, Nanchang 330031, China)
資料名： Rare Metal Materials and Engineering  (Rare Metal Materials and Engineering)
巻： 47  号： 3  ページ： 742-747  発行年： 2018年 
JST資料番号： W3519A  ISSN： 1875-5372  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Al_3Ti/ADC12複合材料の微細構造と特性に及ぼすSr改質の影響を研究した。複合材料の微細構造と破面を光学顕微鏡とSEMで調べた。結果は,Srの添加がα-Al第一相とAl_3Ti粒子のサイズを減少させ,複合材料の形態を変化させることを示した。Sr含有量の最適レベルは0.25wt%であり,共晶シリコンは針状または短棒形状から顆粒状に変化した。一次α-A1相の粗いデンドライトは完全に微細化されている。結果は,Sr添加が機械的性質の改善をもたらすことも示した。マトリックス合金と比較して,Sr添加が0.25wt%のとき,複合材料の引張強さと伸びは,それぞれ36.9%と58%増加した。さらに,破面検査によると,0.25wt%のSrを添加したAl_3Ti/ADC12複合材料からは,へき開面と脆い平坦域はほとんど見られなかった。ディンプルは量が増加し,サイズが減少し,より深く,よく分布した。破壊外観は引張特性の傾向と一致した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 伸び ,  樹枝状結晶 ,  共晶 ,  *ストロンチウム ,  アルミニウム ,  精密化 ,  合金 ,  破面 ,  ケイ素 ,  引張強さ ,  単相 ,  *微細構造 ,  破面検査 ,  *複合材料
準シソーラス用語： ディンプル ,  ADC12 , 【Automatic Indexing@JST】

著者キーワード (5件)： SR改質 ,  Al_3Ti/ADC_12複合材料 ,  微細構造 ,  機械的性質 ,  破壊

分類 (2件)： 機械的性質  (WB02030U) ,  分散強化合金  (WE04030R)

タイトルに関連する用語 (5件)： 複合材料 ,  微細構造 ,  機械的性質 ,  Sr ,  改質