蒸気輸送平衡法による厚い化学量論的リチウム結晶の調製とキャラクタリゼーション【JST・京大機械翻訳】

Preparation and characterization of thick stoichiometric lithium tantalate crystals by vapor transport equilibration method

著者 (8件)： Yang Jinfeng (School of Science, Henan Institute of Engineering, Zhengzhou 451191,China) ,  Mao Qianhui (School of Science, Henan Institute of Engineering, Zhengzhou 451191,China) ,  Shang Jifang (School of Physics, Nankai University, Tianjin 300071, China) ,  Hao Haoshan (School of Science, Henan Institute of Engineering, Zhengzhou 451191,China) ,  Li Qinglian (School of Physics, Nankai University, Tianjin 300071, China) ,  Huang Cunxin (Beijing Sinoma Synthetic Crystals Co., Ltd., Beijing 100018, China) ,  Zhang Ling (School of Physics, Nankai University, Tianjin 300071, China) ,  Sun Jun (School of Physics, Nankai University, Tianjin 300071, China)
資料名： Materials Letters  (Materials Letters)
巻： 232  ページ： 150-152  発行年： 2018年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 改良蒸気輸送平衡(VTE)法を用いて,厚さ3.2mm,直径約56mmの化学量論的タンタル酸リチウム(SLT)結晶を調製した。SLT結晶の化学組成は約49.99mol%である。半径方向に沿った組成の深さ分布と均一性を特性化した。全ウエハの組成偏差は0.02mol%以下であった。SLT結晶の強誘電分域反転に対するポーリング場を,液体電極を用いてランプ電圧を印加することにより測定した。順方向と逆方向のポーリング電界はそれぞれ159V/mmと145V/mmであり,全体のSLT結晶におけるそれらの均一性は有望である。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 電圧 ,  *結晶 ,  電場 ,  *化学量論 ,  深さ分布 ,  *キャラクタリゼーション ,  分極 ,  平衡法 ,  タンタル酸リチウム ,  結晶成長 ,  半径方向 ,  強誘電分域 ,  化学組成
準シソーラス用語： 液体電極 , 【Automatic Indexing@JST】

著者キーワード (5件)： 結晶成長 ,  拡散 ,  化学量論的リチウム ,  VTE法 ,  分極場

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (7件)： 蒸気 ,  輸送 ,  平衡法 ,  リチウム ,  結晶 ,  調製 ,  キャラクタリゼーション