銅合金の微生物腐食抑制のための双性イオン分子層【JST・京大機械翻訳】

Zwitterionic molecule layer for inhibiting microbial corrosion of copper alloy

著者 (5件)： Xu Fengling (State Key Laboratory for Marine Corrosion and Protection, Luoyang Ship Material Research Institute, Qingdao, China) ,  Qiu Zhenghui (State Key Laboratory for Marine Corrosion and Protection, Luoyang Ship Material Research Institute, Qingdao, China) ,  Qiu Ri (State Key Laboratory for Marine Corrosion and Protection, Luoyang Ship Material Research Institute, Qingdao, China and Key Laboratory of Marine Environmental Corrosion and Bio-fouling, Institute of Oceanology, Chinese Academy of Sciences, Qingdao, China) ,  Yang Jiadong (State Key Laboratory for Marine Corrosion and Protection, Luoyang Ship Material Research Institute, Qingdao, China) ,  Lin Cunguo (State Key Laboratory for Marine Corrosion and Protection, Luoyang Ship Material Research Institute, Qingdao, China)
資料名： Anti-Corrosion Methods and Materials  (Anti-Corrosion Methods and Materials)
巻： 65  号： 1  ページ： 46-52  発行年： 2018年 
JST資料番号： B0322A  ISSN： 0003-5599  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 目的:海水中の硫酸塩還元細菌(SRB)により誘導される生物腐食を緩和するために,ポリ(スルホベタインメタクリレート)の双性イオン分子層(ZML)を化学蒸着と表面開始原子移動ラジカル重合によりB10表面上にグラフト化した。設計/方法論/アプローチ:エネルギー分散分光減衰全反射Fourier変換赤外分光法と静的接触角測定を用いて,形成された層を特性化した。表面改質後,B10はSRB接着を有意に減少させ,良好な防汚特性を示した。さらに,生物腐食抑制を動電位分極と電気化学インピーダンス分光法により調べ,ZMLが約90%の抑制効率で生物腐食に対して高い抵抗性を示すことを示した。独創性/価値:ZMLは,生物腐食抑制のための二重の特徴,すなわち防汚膜と腐食抑制剤を実行する。Copyright 2018 Emerald Publishing Limited All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 表面改質 ,  細菌 ,  *腐食抑制作用 ,  移植片 ,  *双性イオン ,  接着 ,  *銅合金 ,  腐食抑制剤 ,  *腐食 ,  *生物腐食 ,  海水 ,  キャラクタリゼーション ,  接触角
準シソーラス用語： 動電位分極 ,  汚損防止 , 【Automatic Indexing@JST】

著者キーワード (4件)： 腐食 ,  腐食抑制 ,  硫酸還元細菌 ,  双性イオン分子層