規則的および長いTiO_2ナノチューブアレイの形成のための室温での酸性溶液中の純Ti箔の電解研磨への新しいアプローチ【JST・京大機械翻訳】

A new approach to electropolishing of pure Ti foil in acidic solution at room temperature for the formation of ordered and long TiO₂ nanotube arrays

著者 (6件)： Asgari Vajihe (Department of Physics, University of Kashan, Kashan 87317-51167, Iran) ,  Noormohammadi Mohammad (Department of Physics, University of Kashan, Kashan 87317-51167, Iran) ,  Ramazani Abdolali (Department of Physics, University of Kashan, Kashan 87317-51167, Iran) ,  Ramazani Abdolali (Institute of Nanoscience and Nanotechnology, University of Kashan, Kashan 87317-51167, Iran) ,  Kashi Mohammad Almasi (Department of Physics, University of Kashan, Kashan 87317-51167, Iran) ,  Kashi Mohammad Almasi (Institute of Nanoscience and Nanotechnology, University of Kashan, Kashan 87317-51167, Iran)
資料名： Corrosion Science  (Corrosion Science)
巻： 136  ページ： 38-46  発行年： 2018年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 酸性溶液中のRTでのTi箔のEPプロセスに対する効果的なアプローチを開発した。このアイデアは,電流密度を最適化するために箔の両側に対して2つの異なる温度(3°CとRT)を用いることである。RTで電解質を保ちながら,低温を箔の背面冷却に用いた。EP条件を最適化した後,Ti表面粗さは約91%減少した。著者らの結果は,TNTsの成長速度が37%まで強化され,非研磨箔と比較して,より大きな面積にわたって配置の著しい改善が観察されることを示した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 成長速度 ,  低温 ,  最適化 ,  電流密度 ,  *研磨 ,  *チタン ,  電解質 ,  *電解研磨
準シソーラス用語： *酸性溶液 ,  *ナノチューブアレイ , 【Automatic Indexing@JST】

著者キーワード (6件)： 電解研磨前処理 ,  Ti ,  粗さ ,  陽極酸化 ,  TiO_2ナノチューブ ,  成長速度