高度に秩序化したSnO_2修飾TiO_2ナノチューブの著しく増強された水素検出【JST・京大機械翻訳】

Remarkably enhanced hydrogen sensing of highly-ordered SnO₂-decorated TiO₂ nanotubes

著者 (4件)： Xun Haitao (State Key Laboratory of Fire Science, Department of Safety Science and Engineering, University of Science and Technology of China, Hefei, Anhui, 230026, PR China) ,  Zhang Zuobin (State Key Laboratory of Fire Science, Department of Safety Science and Engineering, University of Science and Technology of China, Hefei, Anhui, 230026, PR China) ,  Yu Aihua (State Key Laboratory of Fire Science, Department of Safety Science and Engineering, University of Science and Technology of China, Hefei, Anhui, 230026, PR China) ,  Yi Jianxin (State Key Laboratory of Fire Science, Department of Safety Science and Engineering, University of Science and Technology of China, Hefei, Anhui, 230026, PR China)
資料名： Sensors and Actuators. B. Chemical  (Sensors and Actuators. B. Chemical)
巻： 273  ページ： 983-990  発行年： 2018年 
JST資料番号： T0967A  ISSN： 0925-4005  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 高度に秩序化したTiO_2ナノチューブを陽極酸化により調製し,容易な含浸法によりSnO_2ナノ粒子で修飾した。SnO_2負荷は,TiO_2ナノチューブのH_2ガス検知性能を著しく強化した。5mMの濃度の前駆体を含浸した試料は最高の応答と最低の操作温度を示し,250°Cで1410~1000ppmのH_2の30倍の増加応答を達成した。さらに,著しく改善されたH_2選択性と応答/回収速度も得られた。応答時間はべき乗則関係を通してH_2濃度の増加とともに減少したが,応答時間は減少した。約120ppm以上で異なるべき乗則指数が観測され,センシング機構の変化を示唆した。SnO_2@TiO_2ナノチューブの優れたセンシング性能はナノチューブの独特の形態とヘテロ接合の形成に起因した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： ヘテロ接合 ,  アノード酸化 ,  ガスセンサ ,  含浸 ,  *ナノチューブ ,  前駆体 ,  *水素 ,  ナノ粒子 ,  応答時間
準シソーラス用語： 感知機構 ,  べき乗則 ,  ガス検知 , 【Automatic Indexing@JST】

著者キーワード (5件)： TiO_2ナノチューブ ,  ヘテロ接合 ,  水素 ,  ガスセンサ ,  ナノ構造

分類 (2件)： 分析機器  (CC02020S) ,  原子・分子のクラスタ  (BH09030O)

タイトルに関連する用語 (5件)： 秩序化 ,  修飾 ,  ナノチューブ ,  増強 ,  水素