Sr_2SiO_4マトリックス中の還元雰囲気下でのEu3+安定化における補償欠陥の役割【JST・京大機械翻訳】

The role of compensation defects in Eu³⁺ stabilization under reductive atmosphere in Sr₂SiO₄ matrix

著者 (4件)： Szczodrowski Karol (Institute of Experimental Physics, Faculty of Mathematics, Physics and Informatics, University of Gdansk, Wita Stwosza 57, 80-952 Gdansk, Poland) ,  Barzowska Justyna (Institute of Experimental Physics, Faculty of Mathematics, Physics and Informatics, University of Gdansk, Wita Stwosza 57, 80-952 Gdansk, Poland) ,  Gorecka Natalia (Institute of Experimental Physics, Faculty of Mathematics, Physics and Informatics, University of Gdansk, Wita Stwosza 57, 80-952 Gdansk, Poland) ,  Grinberg Marek (Institute of Experimental Physics, Faculty of Mathematics, Physics and Informatics, University of Gdansk, Wita Stwosza 57, 80-952 Gdansk, Poland)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 748  ページ： 44-50  発行年： 2018年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ユウロピウムイオンの発光特性における共ドーパントの役割を研究するために,一定濃度のユウロピウムをドープし,種々の濃度のナトリウム,リチウム,およびホウ素を共ドープしたケイ酸ストロンチウムに基づく発光材料を合成した。得られた材料を粉末X線回折(XRD)法を用いて特性化した。光学測定の結果は,ナトリウムまたはリチウムの取り込みがEu3+の発光強度を増加させるが,還元(5%H_2/N_2)雰囲気下でEu3+を安定化せず,ホウ素共ドーピングで観察されることを示した。さらに,ナトリウムまたはリチウムの共ドーピングがEu3+→Eu2+の還元過程を促進することを示した。得られた結果は,拡散律速過程が合成の還元段階におけるEu3+の安定化に重要であることを示唆した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： ケイ酸ストロンチウム ,  ナトリウム ,  ホウ素 ,  *ユウロピウム ,  ドーパント ,  X線回折 ,  ドーピング ,  光学的測定 ,  リチウム ,  *還元
準シソーラス用語： 共ドーピング ,  発光強度 ,  粉末X線回折 ,  発光特性 ,  ユウロピウムイオン , 【Automatic Indexing@JST】

著者キーワード (4件)： Eu2+/Eu3+ルミネセンス ,  電荷補償欠陥 ,  オルトケイ酸ストロンチウム ,  欠陥マイグレーション

分類 (1件)： 無機化合物のルミネセンス  (BM08093J)

タイトルに関連する用語 (6件)： マトリックス ,  還元雰囲気 ,  安定化 ,  補償 ,  欠陥 ,  役割