Heat-counteracted strategy for tailoring the cell structure and properties of sustainable poly(butylene succinate) foams

著者 (6件)： Yue Jun-Feng (School of Chemistry and Chemical Engineering, Southwest University, Chongqing, 400715, People’s Republic of China) ,  Gan Lin (School of Chemistry and Chemical Engineering, Southwest University, Chongqing, 400715, People’s Republic of China) ,  Liu Chang-Hua (School of Chemistry and Chemical Engineering, Southwest University, Chongqing, 400715, People’s Republic of China) ,  Ma Xiao-Zhou (School of Chemistry and Chemical Engineering, Southwest University, Chongqing, 400715, People’s Republic of China) ,  Wang Dong (Hubei Key Laboratory of Advanced Textile Materials & Application, Wuhan Textile University, Wuhan, 430200, People’s Republic of China) ,  Huang Jin (School of Chemistry and Chemical Engineering, Southwest University, Chongqing, 400715, People’s Republic of China)
資料名： Polymer  (Polymer)
巻： 155  ページ： 50-57  発行年： 2018年 
JST資料番号： D0472B  ISSN： 0032-3861  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 低い溶融強度を有する持続可能なポリブチレンサクシネート(PBS)は,発泡プロセスの間,アゾジカルボアミド(AC)から深刻な熱放出を受け,セル崩壊と低い特性をもたらした。ここでは,吸熱膨張性ミクロスフェア(EnEM)の吸熱効果を利用することにより,AC分解から発熱効果を打ち消すために熱対抗戦略を開発した。PBSの発泡プロセスの間,ACからの熱放出を,EnEM/AC負荷比を最適化することによって調整し,関連理論計算を確立した。PBS発泡体の閉鎖細胞画分は21%からほぼ100%に改善された。PBS発泡体の熱伝導率は58から22mW/(m K)に減少した。さらに,曲げ強さは3から21MPaに増加し,曲げ弾性率は106から278MPaに増加した。この戦略は理論と実践において実行可能であることを検証した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 曲げ強さ ,  熱影響 ,  熱伝導率 ,  ミクロスフェア ,  *ポリブチレンサクシネート ,  細胞構成体 ,  *気泡 ,  最適化 ,  熱放射
準シソーラス用語： 曲げ弾性係数 ,  理論計算 ,  溶融強度 ,  *発泡体 , 【Automatic Indexing@JST】