Study of dry sliding wear characteristics of stellite 6B versus AISI M2 steel at various sliding velocities

著者 (19件)： Gao Wen (Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Gao Wen (Beijing Key Laboratory for Corrosion, Erosion and Surface Technology, Beijing 100083, China) ,  Lian Yong (Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Lian Yong (Beijing Key Laboratory for Corrosion, Erosion and Surface Technology, Beijing 100083, China) ,  Xie Guoliang (State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083, China) ,  Huang Jinfeng (State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083, China) ,  Zhang Le (Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Zhang Le (Beijing Key Laboratory for Corrosion, Erosion and Surface Technology, Beijing 100083, China) ,  Ma Minyu (Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Ma Minyu (Beijing Key Laboratory for Corrosion, Erosion and Surface Technology, Beijing 100083, China) ,  Zhao Chao (Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Zhao Chao (Beijing Key Laboratory for Corrosion, Erosion and Surface Technology, Beijing 100083, China) ,  Zhang Zunjun (State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083, China) ,  Liu Kai (Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Liu Kai (Beijing Key Laboratory for Corrosion, Erosion and Surface Technology, Beijing 100083, China) ,  Zhang Shuguang (Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Zhang Shuguang (Beijing Key Laboratory for Corrosion, Erosion and Surface Technology, Beijing 100083, China) ,  Zhang Jin (Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Zhang Jin (Beijing Key Laboratory for Corrosion, Erosion and Surface Technology, Beijing 100083, China)
資料名： Wear  (Wear)
巻： 402-403  ページ： 169-178  発行年： 2018年 
JST資料番号： E0377A  ISSN： 0043-1648  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 種々の滑り速度(0.95~4.71m/s)での乾燥滑りにおけるステライト6b対AISIM2鋼の摩耗性能は,両ピンとディスクのデブリ,摩擦層と摩耗表面のピンオンディスク摩耗試験と解析により系統的に調べた。ピンとディスクの機械的性能は,高温硬さ試験によって研究した。結果は,ステライト6Bはステライト6B合金/鋼トライボシステムにおける滑り速度の増加に伴って重度から軽度摩耗遷移を受けることを示した。摩耗表面の温度は,速度と負荷の増加に伴って増加し,摩耗表面の酸化とピンとディスクの機械的強度の変化をもたらした。表面状態よりもむしろ摩耗遷移に影響する機械的強度の変動があった。ステライト6B合金の臨界転移滑り速度が2.51m/sであり,これは二領域に滑り速度を分けた。速度は0.95 2.51間のm/sであった時,摩耗メカニズムは,アブレシブ摩耗および剥離摩耗から凝着摩耗に徐々に摩耗速度の減少をもたらした。地域における滑り速度は2.51m/s以上であったことが,酸化摩耗が支配的で,摩耗速度は機械的混合層(MML)の形成のために減少した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 摩耗速度 ,  *摩耗特性 ,  *摩耗 ,  機械的強度 ,  円板 ,  *ステライト ,  *鋼 ,  摩耗試験 ,  アブレシブ摩耗 ,  *滑り速度
準シソーラス用語： 凝着摩耗 ,  摩耗機構 ,  摩耗面 ,  *乾燥滑り ,  *AISIM2 , 【Automatic Indexing@JST】

著者キーワード (4件)： 乾燥滑り ,  ステライト合金 ,  摩擦層 ,  摩耗転移

分類 (2件)： 機械的性質  (WB02030U) ,  潤滑一般  (QB02010S)

タイトルに関連する用語 (5件)： 滑り速度 ,  AISIM2 ,  乾燥滑り ,  摩耗特性 ,  研究