誘導加熱を用いた反応焼結によるMgAl_2O_4/YAG共晶複合材料のその場調製【JST・京大機械翻訳】

The In Situ Preparation of MgAl₂O₄/YAG Eutectic Composites by Reaction Sintering Using Induction Heating

著者 (5件)： Xu Huan (Wuhan University of Science and Technology, State Key Laboratory Cultivation Base of Refractories and Ceramics; Wuhan, China, 430081) ,  Wang Xi Tang (Wuhan University of Science and Technology, State Key Laboratory Cultivation Base of Refractories and Ceramics; Wuhan, China, 430081) ,  Wang Zhou Fu (Wuhan University of Science and Technology, State Key Laboratory Cultivation Base of Refractories and Ceramics; Wuhan, China, 430081) ,  Ma Yan (Wuhan University of Science and Technology, The State Key Laboratory of Refractories and Metallurgy; Wuhan, China, 430081) ,  Liu Hao (Wuhan University of Science and Technology, The State Key Laboratory of Refractories and Metallurgy; Wuhan, China, 430081)
資料名： Solid State Phenomena  (Solid State Phenomena)
巻： 281  ページ： 111-117  発行年： 2018年 
JST資料番号： T0583A  ISSN： 1012-0394  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： スイス (CHE)  言語： 英語 (EN)

抄録/ポイント： 高密度MgAl_2O_4/YAG(イットリウムアルミニウムガーネット)共晶複合材料を,誘導加熱(IH)を用いたその場反応焼結によって首尾よく調製した。IH時間と出発材料組成が相組成と微細構造に及ぼす影響を調べた。結果は,11.54の間のAl_2O_3/MgO比の範囲において,短時間において,MgAl_2O_4とYAG相だけから成る共晶複合材料を,IHによって調製することができることを示した。従来の焼結(CS)と比較して,スピネルにおけるAl_2O_3の溶解度は,高温と誘導電磁場の相乗効果の下で著しく強化される。より高いYAG含有量はより多くの共晶液相の形成を容易にし,より均一でより密な相互貫入ネットワーク構造を得るのに好都合である。Copyright 2018 Trans Tech Publications Ltd. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： アルミニウム ,  *共晶 ,  *複合材料 ,  微細構造 ,  酸化マグネシウム ,  ネットワーク構造 ,  スピネル ,  電磁場 ,  *焼結 ,  相組成 ,  高温 ,  *反応焼結 ,  液相 ,  イットリウムアルミニウムガーネット ,  *誘導加熱
準シソーラス用語： その場反応 , 【Automatic Indexing@JST】

著者キーワード (4件)： 溶解度 ,  誘導加熱 ,  微細構造 ,  MgAl_2O_4-YAG複合材料

分類 (1件)： セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (6件)： 誘導加熱 ,  反応焼結 ,  YAG ,  共晶 ,  複合材料 ,  調製