架橋中及び後の二成分ポリウレタンエラストマの化学,高分子動力学及び機械的性質 II 湿潤条件【JST・京大機械翻訳】

Chemistry, polymer dynamics and mechanical properties of a two-part polyurethane elastomer during and after crosslinking. Part II: moist conditions

著者 (5件)： Zimmer Bettina (Adhesion and Interphases in Polymers, Saarland University, PB 151150, Campus C 6.3, D-66041, Saarbruecken, Germany) ,  Nies Christophe (Adhesion and Interphases in Polymers, Saarland University, PB 151150, Campus C 6.3, D-66041, Saarbruecken, Germany) ,  Schmitt Christian (Adhesion and Interphases in Polymers, Saarland University, PB 151150, Campus C 6.3, D-66041, Saarbruecken, Germany) ,  Paulo Cristo (Adhesion and Interphases in Polymers, Saarland University, PB 151150, Campus C 6.3, D-66041, Saarbruecken, Germany) ,  Possart Wulff (Adhesion and Interphases in Polymers, Saarland University, PB 151150, Campus C 6.3, D-66041, Saarbruecken, Germany)
資料名： Polymer  (Polymer)
巻： 149  ページ： 238-252  発行年： 2018年 
JST資料番号： D0472B  ISSN： 0032-3861  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,2部ポリウレタンシステムの特性に及ぼす製造条件(硬化手順,水分)の影響を検討した。パートIは乾燥条件における硬化と貯蔵中の化学的,誘電的及び機械的性質を扱うが,この第二部は湿潤条件におけるカロリーガラス転移と共に,硬化後の異なる時間に導入された水分を含むこれらの性質に焦点を当てた。製造中の水の存在は,イソシアナート(第一アミンと尿素を形成する)と反応することにより最終特性(ポリマ移動度の増加,機械的剛性の低下)に大きく影響し,それにより非臨界湿度条件に対してさえ架橋密度を低下させることを示した。水分を含む他の化学的副反応も同定した。水はさらに高分子動力学を加速する。全体として,硬化と貯蔵中の水分はPUの特性変化の原因として明確に同定された。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 移動度 ,  ガラス転移 ,  重合体 ,  剛性 ,  湿度 ,  架橋度 ,  *湿潤 ,  水分 ,  臨界 ,  イソシアン酸塩 ,  副反応 ,  *分子動力学 ,  第一アミン ,  ウレア化合物

著者キーワード (7件)： ポリウレタン ,  架橋 ,  成熟 ,  水分 ,  FTIR-ATR分光法 ,  誘電スペクトロスコピー ,  引張試験