粒子制御による高効率赤色発光Ca_14Zn_6Al_9.97Mn_0.03O_35蛍光体の合成【JST・京大機械翻訳】

Synthesis of high-efficiency red-emission Ca₁₄Zn₆Al_9.97Mn_0.03O₃₅ phosphors with particle control

著者 (6件)： Hur Man Gyu (Sungkyunkwan University, School of Advanced Materials Science & Engineering, Suwon 16419, Republic of Korea) ,  Choi Seung Hee (Sungkyunkwan University, School of Advanced Materials Science & Engineering, Suwon 16419, Republic of Korea) ,  Kwon Seok Bin (Sungkyunkwan University, School of Advanced Materials Science & Engineering, Suwon 16419, Republic of Korea) ,  Masaki Takaki (Sungkyunkwan University, School of Advanced Materials Science & Engineering, Suwon 16419, Republic of Korea) ,  Toda Kenji (Graduate School of Science and Technology, Niigata University, 8050 Ikarashi 2-nocho, Niigata 950-2181, Japan) ,  Yoon Dae Ho (Sungkyunkwan University, School of Advanced Materials Science & Engineering, Suwon 16419, Republic of Korea)
資料名： Ceramics International  (Ceramics International)
巻： 44  号： 13  ページ： 15868-15872  発行年： 2018年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 液相前駆体(LPP)法を用いて,ナノからミクロンサイズまでの種々のサイズの粒子を有する高効率Ca_14Zn_6Al_9.97-Mn_0.03O_35(CZAMO)赤色蛍光体を合成した。1000°Cで得られたCZAMO蛍光体の粒径は150nm以下であったが,焼成温度の上昇と共にミクロンサイズに成長した。CZAMO蛍光体の赤色発光波長範囲は,713nm発光ピーク(450nmで励起)を有する650~750nmであった。LPP法(L-CZAMO)により合成したCZAMO蛍光体を固相反応(SSR)法(S-CZAMO)により合成したCZAMO蛍光体と比較した場合,L-CZAMOの光ルミネセンス(PL)強度は1000°C(1200°C)でS-CZAMOのそれよりも4倍大きかった(14%高い)。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 粒径 ,  前駆体 ,  *発光 ,  光ルミネセンス ,  液相 ,  固相反応 ,  励起 ,  *蛍光体
準シソーラス用語： 波長領域 ,  焼成温度 ,  赤色蛍光体 ,  ミクロンサイズ ,  *赤色発光 ,  *高効率 , 【Automatic Indexing@JST】

著者キーワード (5件)： Ca_14Zn_6Al_9.97Mn_0.03O_35 ,  赤色蛍光体 ,  液相前駆体法 ,  粒子制御 ,  光ルミネセンス