ゴールデン合金Cu5Zn5Al1Sn:マルチ分析表面キャラクタリゼーション【Powered by NICT】

The golden alloy Cu-5Zn-5Al-1Sn: A multi-analytical surface characterization

著者 (5件)： Chang Tingru (National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing, 100083, China) ,  Chang Tingru (KTH Royal Institute of Technology, Division of Surface and Corrosion Science, School of Chemical Science and Engineering, SE 10044, Stockholm, Sweden) ,  Wallinder Inger Odnevall (KTH Royal Institute of Technology, Division of Surface and Corrosion Science, School of Chemical Science and Engineering, SE 10044, Stockholm, Sweden) ,  Jin Ying (National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing, 100083, China) ,  Leygraf Christofer (KTH Royal Institute of Technology, Division of Surface and Corrosion Science, School of Chemical Science and Engineering, SE 10044, Stockholm, Sweden)
資料名： Corrosion Science  (Corrosion Science)
巻： 131  ページ： 94-103  発行年： 2018年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ゴールデン合金Cu5Zn5Al1Snは変色への出現と抵抗のために多くの応用を見出している。Cu5Zn5Al1Snの微細構造と多成分表面酸化物は多重分析法によって調べた。市販Cu金属と比較して,Cuの5Zn5Al1Snは有意に小さな結晶粒とコヒーレント双晶境界のより高い分率を有している。ダイヤモンド研磨後に形成された5~10nm厚さの酸化物はすべての全体的な耐食性に寄与する四種の同定された亜酸化物を有している。Cu_2Oは主に外側部分,続いてZnO,SnO_2とAl_2O_3合金基板に近いによるに位置している。後三者は障壁特性を有しているが,Cu_2Oはより複雑な構造を示した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 酸化亜鉛 ,  ダイヤモンド ,  結晶粒 ,  コヒーレンス ,  耐食性 ,  双晶境界 ,  多重化 ,  銅 ,  微細構造 ,  研磨 ,  酸化物 ,  *キャラクタリゼーション
準シソーラス用語： 金基板 ,  亜酸化物 ,  表面酸化 , 【Automatic Indexing@JST】

著者キーワード (5件)： 銅合金 ,  B陰極還元 ,  GDOES ,  XPS ,  C大気腐食

分類 (1件)： 腐食  (WB03030B)

タイトルに関連する用語 (3件)： マルチ ,  分析 ,  キャラクタリゼーション