溶融炭酸塩燃料電池用の二重イオン伝導膜【JST・京大機械翻訳】

Dual ionic conductive membrane for molten carbonate fuel cell

著者 (6件)： Baron Robert (Warsaw University of Technology, Faculty of Materials Science and Engineering, Woloska 141 Str., Warsaw, Poland) ,  Wejrzanowski Tomasz (Warsaw University of Technology, Faculty of Materials Science and Engineering, Woloska 141 Str., Warsaw, Poland) ,  Szablowski Lukasz (Warsaw University of Technology, The Institute of Heat Engineering, Nowowiejska 21/25 Str., Warsaw, Poland) ,  Szczesniak Arkadiusz (Warsaw University of Technology, The Institute of Heat Engineering, Nowowiejska 21/25 Str., Warsaw, Poland) ,  Milewski Jaroslaw (Warsaw University of Technology, The Institute of Heat Engineering, Nowowiejska 21/25 Str., Warsaw, Poland) ,  Fung Kuan-Zong (National Cheng Kung University, Department of Materials Science and Engineering, No.1 University Road, Tainan, Taiwan)
資料名： International Journal of Hydrogen Energy  (International Journal of Hydrogen Energy)
巻： 43  号： 16  ページ： 8100-8104  発行年： 2018年 
JST資料番号： B0192B  ISSN： 0360-3199  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究の範囲内で,電気化学的に不活性な溶融炭酸塩燃料電池(MCFC)γ-LiAlO_2マトリックスを,固体酸化物燃料電池(SOFC)応用に典型的な酸素イオン伝導性セラミックによって置き換えた。このような溶液は溶融炭酸塩混合物(CO_32-)とイットリア安定化ジルコニア(YSZ)またはサマリアドープセリア(SDC)マトリックス(O2-)の両方による相乗的イオン輸送をもたらす。単一単位セル試験により,ハイブリッドイオン膜の適用が,広範囲の動作温度(600°C~750°C)に対して,純粋なγ-LiAlO_2上のMCFCの性能(電力密度)を増加させることを確認した。SDCとYSZマトリックスによるセル出力密度は,MCFCの典型的650°C動作温度におけるγ-LiAlO_2と比較して,それぞれ2%と13%高かった。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： セラミック ,  イオン輸送 ,  電気化学 ,  ドーピング ,  固体酸化物燃料電池 ,  *炭酸塩 ,  *イオン伝導 ,  酸化セリウム
準シソーラス用語： 出力密度 ,  電力密度 ,  動作温度 ,  YSZ【セラミック】 ,  酸素イオン , 【Automatic Indexing@JST】

著者キーワード (5件)： 溶融炭酸塩燃料電池 ,  γ-アルミン酸リチウム ,  サマリアをドープしたセリア ,  イットリア安定化ジルコニア ,  電解質マトリックス

分類 (1件)： 燃料電池  (YB04040V)

タイトルに関連する用語 (2件)： 溶融炭酸塩燃料電池 ,  イオン伝導