磁場_S FeBPSiC非晶質合金の磁気的性質に及ぼすフラックス精製とその効果【Powered by NICT】

Fluxing purification and its effect on magnetic properties of high-B _s FeBPSiC amorphous alloy

著者 (12件)： Pang Jing (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, Liaoning 110870, China) ,  Wang Anding (Key Laboratory of Magnetic Materials and Devices, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang 315201, China) ,  Wang Anding (Center for Advanced Structural Materials, Department of Mechanical and Biomedical Engineering, College of Science and Engineering, City University of Hong Kong, Kowloon, Hong Kong, China) ,  Yue Shiqiang (Key Laboratory of Magnetic Materials and Devices, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang 315201, China) ,  Yue Shiqiang (Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China) ,  Kong Fengyu (School of Materials and Chemical Engineering, Ningbo University of Technology, Ningbo 315016, China) ,  Qiu Keqiang (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, Liaoning 110870, China) ,  Chang Chuntao (Key Laboratory of Magnetic Materials and Devices, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang 315201, China) ,  Chang Chuntao (Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China) ,  Wang Xinmin (Key Laboratory of Magnetic Materials and Devices, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang 315201, China) ,  Wang Xinmin (Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China) ,  Liu Chain-Tsuan (Center for Advanced Structural Materials, Department of Mechanical and Biomedical Engineering, College of Science and Engineering, City University of Hong Kong, Kowloon, Hong Kong, China)
資料名： Journal of Magnetism and Magnetic Materials  (Journal of Magnetism and Magnetic Materials)
巻： 433  ページ： 35-41  発行年： 2017年 
JST資料番号： H0644A  ISSN： 0304-8853  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 塩基組成Fe_83B_11P_3Si_2C_1と高磁場_S非晶質合金は工業化における原料で調製した合金の非晶質形成能および磁気的性質に及ぼすフラックス精製の影響を検討した。フラックス精製を用いて,表面結晶化が抑制され,最大厚さ48μmの完全に非晶質Fe_83B_11P_3Si_2C_1リボンは工業プロセスと材料を用いて達成することに成功した。工業用精製合金で製造した非晶質リボンは優れた磁気的性質,高磁場_1.65T,2.0の低いH_C及び1kHzで9.7×10~3の高いμ_e含有を示した。融解合金中の不純物は三種類の形態で存在し,磁気的性質に及ぼす異なるをた。表面結晶化は核として働く高融点包有物として存在する不純物によって引き起こされた。フラックス精製は高磁場_S FeBPSiC非晶質合金の工業化のための実行可能な方法である。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *非晶質 ,  強磁場 ,  工業化 ,  不純物 ,  *磁場 ,  結晶化 ,  *合金 ,  非晶質リボン ,  *非晶質合金 ,  *磁気的性質 ,  包有物

著者キーワード (5件)： 非晶質合金 ,  軟磁気特性 ,  高B_ ,  溶融紡糸 ,  フラックス精製