圧縮エタン下でのスチレンの水性不均一ラジカル重合【JST・京大機械翻訳】

Aqueous heterogeneous radical polymerization of styrene under compressed ethane

著者 (4件)： Nik Hadzir Noor Hadzuin (Department of Food Technology, Faculty of Food Science and Technology, Universiti Putra Malaysia, 43400 Serdang, Selangor, Malaysia) ,  Semciw Matthew (Centre for Advanced Macromolecular Design (CAMD), School of Chemical Engineering, The University of New South Wales, UNSW Sydney, NSW 2052, Australia) ,  Lucien Frank P. (Centre for Advanced Macromolecular Design (CAMD), School of Chemical Engineering, The University of New South Wales, UNSW Sydney, NSW 2052, Australia) ,  Zetterlund Per B. (Centre for Advanced Macromolecular Design (CAMD), School of Chemical Engineering, The University of New South Wales, UNSW Sydney, NSW 2052, Australia)
資料名： Journal of Supercritical Fluids  (Journal of Supercritical Fluids)
巻： 142  ページ： 45-51  発行年： 2018年 
JST資料番号： W1591A  ISSN： 0896-8446  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 圧縮ガスによるエマルションの加圧は,高分子ナノ粒子を製造するために重合できるミニエマルションの調製のための低エネルギールートを提供する可能性がある。通常のアプローチは,ミニエマルションを生成するために高エネルギー混合を必要とし,これはそれらの工業的応用を妨げる。本研究では,スチレン/水および陰イオン界面活性剤Dowfax 8390に基づく水中油(ミニ)エマルションを生成するために,圧縮エタンを用いた。初期の混濁エマルションは60°Cと6MPaで圧縮エタン下で透明になった。これらの条件でのスチレンの水性不均一ラジカル重合により,直径約60nmのナノ粒子が得られた。しかし,機械的研究は,粒子形成が単量体液滴(液滴核形成)の直接重合よりも古典的な乳化重合機構(水性ミセル核形成)により進行することを明らかにした。透明現象は,連続および分散相における整合屈折率に起因する。Lorentz-Lorenz混合則を用いて,透明条件での分散相における屈折率とエタン溶解度の両方を推定した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 乳化重合 ,  単量体 ,  屈折率 ,  液滴 ,  核形成 ,  *ラジカル重合 ,  ナノ粒子 ,  溶解度 ,  乳濁液 ,  ミセル ,  *重合 ,  陰イオン界面活性剤 ,  芳香族炭化水素 ,  ビニル化合物 ,  アルカン
準シソーラス用語： ミニエマルション , 【Automatic Indexing@JST】

著者キーワード (3件)： エタン ,  ミニエマルション ,  ラジカル重合

分類 (2件)： 有機物質からなる多成分系の相平衡・状態図  (CB03016J) ,  抽出  (XD02030B)

物質索引 (2件)： スチレン ,  エタン

タイトルに関連する用語 (4件)： エタン ,  スチレン ,  不均一 ,  ラジカル重合