Magnetic field control of microstructural development in melt-spun Pr 2 Co 14 B

著者 (12件)： McGuire Michael A. (Oak Ridge National Laboratory, Oak Ridge, TN, USA) ,  Rios Orlando (Oak Ridge National Laboratory, Oak Ridge, TN, USA) ,  Conner Ben S. (Oak Ridge National Laboratory, Oak Ridge, TN, USA) ,  Carter William G. (Oak Ridge National Laboratory, Oak Ridge, TN, USA) ,  Huang Mianliang (The Ames Laboratory, Ames, IA, USA) ,  Sun Kewei (The Ames Laboratory, Ames, IA, USA) ,  Palasyuk Olena (The Ames Laboratory, Ames, IA, USA) ,  Jensen Brandt (The Ames Laboratory, Ames, IA, USA) ,  Zhou Lin (The Ames Laboratory, Ames, IA, USA) ,  Dennis Kevin (The Ames Laboratory, Ames, IA, USA) ,  Nlebedim Ikenna C. (The Ames Laboratory, Ames, IA, USA) ,  Kramer Matthew J. (The Ames Laboratory, Ames, IA, USA)
資料名： Journal of Magnetism and Magnetic Materials  (Journal of Magnetism and Magnetic Materials)
巻： 430  ページ： 85-88  発行年： 2017年 
JST資料番号： H0644A  ISSN： 0304-8853  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 商用希土類永久磁石の処理では,外部磁場の使用は,異方性粒子の整列と終了磁石の分極に主に限定されている。磁石合成の初期段階に及ぼす高磁場の影響,Pr-Co-B系における2:14:1相を生成する結晶化と化学的相変態を調べた。メルトスピニングにより製造したPr2Co14B合金は強い印加磁場(H=90kOe)の存在下でアニールした。得られた材料を,X線回折,電子顕微鏡,および磁化測定によって特性化した。磁場は結晶相の核形成と成長を抑制し,有意に小さい粒径をもたらすことを見出した。添加は,加工の際に印加磁場が強く化学相選択に影響を及ぼし,Pr2Co17のPr2Co14Bとα-Coの形成を抑制した。結果は,重要な微細構造特性の制御の増加は希土類磁石材料の加工パラメータとして強磁場を含めることにより達成可能であることを示した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 核形成 ,  強磁場 ,  外部磁場 ,  異方性 ,  磁化特性測定 ,  永久磁石 ,  X線回折 ,  *溶融紡糸 ,  結晶化 ,  単相 ,  磁石 ,  *微細構造 ,  *磁場
準シソーラス用語： 希土類磁石 ,  印加磁場 , 【Automatic Indexing@JST】

分類 (1件)： 金属結晶の磁性  (BM06040T)

タイトルに関連する用語 (4件)： 溶融紡糸 ,  微細構造 ,  発達 ,  磁場