CrおよびSi被毒条件下でのLa_2NiO_4+δの相分解【JST・京大機械翻訳】

Phase decomposition of La₂NiO_4+δ under Cr- and Si-poisoning conditions

著者 (6件)： Schrodl N. (Chair of Physical Chemistry, Montanuniversitaet Leoben, Franz-Josef-Strasse 18, 8700 Leoben, Austria) ,  Egger A. (Chair of Physical Chemistry, Montanuniversitaet Leoben, Franz-Josef-Strasse 18, 8700 Leoben, Austria) ,  Gspan C. (Institute for Electron Microscopy and Nanoanalysis (FELMI), Graz University of Technology, Graz Centre for Electron Microscopy (ZFE), Steyrergasse 17, 8010 Graz, Austria) ,  Hoschen T. (Max Planck Institute for Plasma Physics, Boltzmannstrasse 2, 85748 Garching, Germany) ,  Hofer F. (Institute for Electron Microscopy and Nanoanalysis (FELMI), Graz University of Technology, Graz Centre for Electron Microscopy (ZFE), Steyrergasse 17, 8010 Graz, Austria) ,  Sitte W. (Chair of Physical Chemistry, Montanuniversitaet Leoben, Franz-Josef-Strasse 18, 8700 Leoben, Austria)
資料名： Solid State Ionics  (Solid State Ionics)
巻： 322  ページ： 44-53  発行年： 2018年 
JST資料番号： B0096B  ISSN： 0167-2738  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： La_2NiO_4+δの酸素交換動力学に及ぼす同時Cr-およびSi-被毒の影響を,DC-伝導率緩和測定によって4000時間の期間にわたって乾燥および湿潤O_2/Ar雰囲気中で800°Cで研究した。X線光電子分光法(XPS)深さプロファイリング,エネルギー分散X線分光法による走査電子顕微鏡(SEM-EDXS)およびエネルギー分散X線および電子エネルギー損失分光法を用いた高分解能走査透過型電子顕微鏡(HR-STEM EDXS/EELS)を用いて,ますます過酷な環境条件に曝されたLa_2NiO_4+δ表面の化学的および形態的変化を調べた。Cr/Si源の存在および乾燥条件下で,La_2NiO_4+δは1000時間以上の良好な安定性を示した。しかし,湿度がシステムに導入されるとすぐに,酸素交換活性の強い低下が観察された。試験後の分析により,酸素の表面交換を妨げるLa_2NiO_4+δの表面上に,新たに形成された部分的ブロッキングCrおよびSiリッチ二次相が明らかになった。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 走査電子顕微鏡 ,  エネルギー分散X線分光分析 ,  第二相 ,  ブロッキング ,  湿度 ,  湿潤 ,  *クロム ,  X線光電子分光法 ,  深さプロフィル ,  酸素 ,  X線 ,  *中毒 ,  エネルギー散逸 ,  高分解能

著者キーワード (4件)： SOFCカソード ,  Cr中毒 ,  SI中毒 ,  劣化