スパークプラズマ焼結により作製したMnBi磁石の保磁力に及ぼす粒界相の影響【JST・京大機械翻訳】

Effects of intergranular phase on the coercivity for MnBi magnets prepared by spark plasma sintering

著者 (7件)： Cao J. (School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, P.R. China) ,  Huang Y. L. (School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, P.R. China) ,  Hou Y. H. (School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, P.R. China) ,  Zhang G. Q. (School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, P.R. China) ,  Shi Z. Q. (School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, P.R. China) ,  Zhong Z. C. (Jiangxi Key Laboratory for Rare Earth Magnetic Materials and Devices, Jiangxi University of Science and Technology, Ganzhou 341000, P.R. China) ,  Liu Z. W. (School of Materials Science and Engineering, South China University of Technology, Guangzhou 510640, P.R. China)
資料名： AIP Advances (Web)  (AIP Advances (Web))
巻： 8  号： 5  ページ： 055132-055132-7  発行年： 2018年 
JST資料番号： U7121A  ISSN： 2158-3226  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 低温相(LTP)の高含有量と優れた磁気特性を有するMnBi磁石を,磁気精製なしの前駆体としてボールミル粉砕粉末を用いたスパークプラズマ焼結(SPS)によって調製した。MnBi磁石中にMn相,Bi相,MnO相および非晶質相を含む複雑な粒界相を特性化し,系統的に報告した。ボールミル粉砕前駆体と焼結機構により寄与される粒界相の形成が磁気特性に重要な影響を持つことが分かった。粒間相の適切な含有量は,強い磁気分離効果により保磁力を改善するのに有益であった。室温でのM_r=26.0emu/g,H_ci=7.11kOeおよび(BH)_max=1.53MGOeの最適磁気特性および550Kでの最大値H_ci=25.37kOeを得ることができた。強い好ましい磁気特性は,SPSed MnBi磁石を高温応用に使用される小型永久磁石用の魅力的な候補材料にする。(翻訳著者抄録)【JST・京大機械翻訳】

シソーラス用語： *マンガン ,  磁気 ,  磁力分離 ,  低温 ,  永久磁石 ,  高温 ,  *放電プラズマ焼結 ,  前駆体 ,  粉体 ,  キャラクタリゼーション ,  *保磁力 ,  *磁石 ,  *ビスマス ,  *焼結
準シソーラス用語： ボールミル摩砕 , 【Automatic Indexing@JST】

分類 (3件)： 電磁石  (NA05080G) ,  金属結晶の磁性  (BM06040T) ,  磁性材料  (NA04040H)

タイトルに関連する用語 (5件)： スパークプラズマ焼結 ,  作製 ,  磁石 ,  保磁力 ,  粒界相