TiドープAl_2O_3ナノ複合セラミック被覆したCPチタンインプラント材料の摩耗および腐食特性に及ぼすTi量の影響【Powered by NICT】

Effect of Ti amount on wear and corrosion properties of Ti-doped Al₂O₃ nanocomposite ceramic coated CP titanium implant material

著者 (5件)： Comakli O. (Erzurum Technical University, Faculty of Engineering and Architecture, Department of Mechanical Engineering, Erzurum, Turkey) ,  Yazici M. (Erzurum Technical University, High Technology Research Centre, Erzurum, Turkey) ,  Yetim T. (Erzurum Technical University, Faculty of Engineering and Architecture, Department of Chemical Engineering, Erzurum, Turkey) ,  Yetim A.F. (Erzurum Technical University, Faculty of Engineering and Architecture, Department of Mechanical Engineering, Erzurum, Turkey) ,  Celik A. (Ataturk University, Faculty of Engineering, Department of Mechanical Engineering, Erzurum, Turkey)
資料名： Ceramics International  (Ceramics International)
巻： 44  号： 7  ページ： 7421-7428  発行年： 2018年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Al_2O_3およびTiドープAl_2O_3ナノ複合材料セラミック被覆はゾル-ゲル浸漬コーティングプロセスを用いて調製した。Ti量に関連してAl_2O_3セラミック皮膜の腐食と摩耗抵抗を,ピン・オン・ディスク摩擦試験機,動電位分極および電気化学インピーダンス分光法(EIS)を用いて行った。腐食と摩耗試験前後の表面特性を走査電子顕微鏡(SEM),X線回折(XRD)と硬さ分析により調べた。腐食と摩耗試験の結果は,ナノ複合材料セラミック皮膜の耐食性と耐摩耗性は非被覆試料より良好になることを示した。,Tiドーピング含有量をもつ改善されたナノ複合体セラミック被覆の耐食性と耐摩耗性は増加した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *摩耗 ,  走査電子顕微鏡 ,  *ナノ複合材料 ,  *腐食 ,  *ドーピング ,  浸漬塗装 ,  表面性状 ,  *チタン ,  *セラミック被覆 ,  耐食性 ,  摩擦試験 ,  耐摩耗性 ,  摩耗試験
準シソーラス用語： 動電位分極 ,  *腐食挙動 , 【Automatic Indexing@JST】

著者キーワード (5件)： ゾル-ゲル ,  Al_2O_3ナノ複合セラミック被覆 ,  Tiドーピング ,  腐食 ,  摩耗