Irradiation effects and beam strength in polyurethane materials for laser elements

著者 (8件)： Kosyanchuk L.F. (Institute of Macromolecular Chemistry NAS of Ukraine, 48 Kharkovskoe av, 02160, Kyiv, Ukraine) ,  Kozak N.V. (Institute of Macromolecular Chemistry NAS of Ukraine, 48 Kharkovskoe av, 02160, Kyiv, Ukraine) ,  Babkina N.V. (Institute of Macromolecular Chemistry NAS of Ukraine, 48 Kharkovskoe av, 02160, Kyiv, Ukraine) ,  Bezrodna T.V. (Institute of Physics NAS of Ukraine, 46 Nauki av, 03680, Kyiv, Ukraine) ,  Roshchin O.M. (Institute of Physics NAS of Ukraine, 46 Nauki av, 03680, Kyiv, Ukraine) ,  Bezrodnyi V.I. (Institute of Physics NAS of Ukraine, 46 Nauki av, 03680, Kyiv, Ukraine) ,  Antonenko O.I. (Institute of Macromolecular Chemistry NAS of Ukraine, 48 Kharkovskoe av, 02160, Kyiv, Ukraine) ,  Brovko O.O. (Institute of Macromolecular Chemistry NAS of Ukraine, 48 Kharkovskoe av, 02160, Kyiv, Ukraine)
資料名： Optical Materials  (Optical Materials)
巻： 85  ページ： 408-413  発行年： 2018年 
JST資料番号： W0468A  ISSN： 0925-3467  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 種々のジイソシアナート及びグリコール成分を用いた重縮合法により合成したポリウレタンの構造特異性及び粘弾性に及ぼす照射の影響を調べた。光酸化過程は,高分子架橋点間の鎖セグメントに対する材料の弾性,ガラス転移温度及び平均分子量を変化させ,アルコール及びヒドロペルオキシド基の形成により系におけるヒドロキシル基の蓄積を誘導することを示した。ポリウレタンのビーム強度は,特に脂肪族ブロックの長さと架橋ネットワークの密度に依存することが分かった。動的機械分析,IR分光法,EPR法および単一パルスレーザ破壊閾値に対するデータにより得られた結果の間の良好な一致は,さらに開発したポリウレタン材料に対する光酸化感受性を予測することを可能にした。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 粘弾性 ,  *レーザ ,  動的機械分析 ,  ネットワーク ,  重縮合 ,  アルコール ,  ガラス転移点 ,  ヒドロキシ基 ,  *ポリウレタン ,  感受性 ,  弾性 ,  パルスレーザ ,  光酸化
準シソーラス用語： ヒドロペルオキシド ,  特異性 , 【Automatic Indexing@JST】

著者キーワード (4件)： ポリウレタン ,  弾性係数 ,  相関時間 ,  ビーム強度

分類 (2件)： 非線形光学  (BD05000T) ,  光デバイス一般  (BD06010L)

タイトルに関連する用語 (4件)： レーザ ,  ポリウレタン材料 ,  照射効果 ,  ビーム強度