焼結炭化物板で強化された選ばれた耕うん機の摩耗抵抗【JST・京大機械翻訳】

Wear resistance of selected cultivator coulters reinforced with sintered-carbide plates

著者 (3件)： Stawicki Tomasz (Department of Agrotechnical Systems Engineering, Faculty of Environmental Management and Agriculture, West Pomeranian University of Technology, Papieza Pawla VI Street 1, 71-459 Szczecin, Poland) ,  Kostencki Piotr (Department of Agrotechnical Systems Engineering, Faculty of Environmental Management and Agriculture, West Pomeranian University of Technology, Papieza Pawla VI Street 1, 71-459 Szczecin, Poland) ,  Bialobrzeska Beata (Department of Materials Science, Welding and Strength of Materials, Faculty of Mechanical Engineering, Wroclaw University of Technology, Smoluchowskiego Street 25, 50-370 Wroclaw, Poland)
資料名： Archives of Civil and Mechanical Engineering  (Archives of Civil and Mechanical Engineering)
巻： 18  号： 4  ページ： 1661-1678  発行年： 2018年 
JST資料番号： W3273A  ISSN： 1644-9665  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 研究の中で,栽培者に使用されるcoulの耐摩耗性を評価した。部品の3つの構成解を調べた。(a)ブレード領域で強化された,(a)ブレード-炭化物板で補強された。(B)鋼-炭化物板を有するブレード領域およびパッド溶接によるそれらの更なる部分において強化された。(C)補強材(均質材料で作られた)はない。検討した部分は,有意な湿度を持つローム-砂土壌の栽培に使用された4ビーム栽培装置に設置された。非強化のものと比較して,焼結炭化物板だけで強化され,付加的なパッド溶接で強化されたものは,アブレシブ摩耗に対する十分に高い抵抗によって特徴付けられた。coulの強化は,それらの限界状態条件の変化をもたらした。焼結炭化物で作られた板は,部品の長さ減少率を減少させた。それは,母材領域におけるそれらの厚さの大きな損失をもたらした。この装置の限界摩耗条件は,結石において打撃するときに破壊されるcoulの曲げ強さ係数の摩擦または減少に関連していた。非強化coulータでは,限界摩耗条件はそれらの長さの過剰な減少から生じた。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 鋼 ,  *焼結 ,  湿度 ,  *炭化物 ,  栽培 ,  アブレシブ摩耗 ,  パッド ,  *摩耗 ,  *耐摩耗性 ,  曲げ強さ ,  ローム ,  溶接 ,  補強材料
準シソーラス用語： 減衰率 ,  限界状態 , 【Automatic Indexing@JST】

著者キーワード (4件)： 摩耗 ,  焼結炭化物 ,  耕うん機coulター ,  SEM

分類 (2件)： 機械的性質  (WB02030U) ,  潤滑一般  (QB02010S)

タイトルに関連する用語 (3件)： 強化 ,  耕うん機 ,  摩耗抵抗