鉛フリー(1-x)Na_0.5Bi_0.5TiO_3-xSr_3(x=0,0.10,0.26)ホイスカの溶融塩合成とキャラクタリゼーション【JST・京大機械翻訳】

Molten salt synthesis and characterization of lead-free (1-x)Na_0.5Bi_0.5TiO₃-xSrTiO₃ (x = 0, 0.10, 0.26) whiskers

著者 (6件)： Zhou Xuefan (State key Laboratory of Powder Metallurgy, Central South University, Changsha, Hunan 410083, China) ,  Wu Zhong (State key Laboratory of Powder Metallurgy, Central South University, Changsha, Hunan 410083, China) ,  Jiang Chao (School of Aeronautics and Astronautics, Central South University, Changsha, Hunan 410083, China) ,  Luo Hang (State key Laboratory of Powder Metallurgy, Central South University, Changsha, Hunan 410083, China) ,  Yan Zhongna (State key Laboratory of Powder Metallurgy, Central South University, Changsha, Hunan 410083, China) ,  Zhang Dou (State key Laboratory of Powder Metallurgy, Central South University, Changsha, Hunan 410083, China)
資料名： Ceramics International  (Ceramics International)
巻： 44  号： 8  ページ： 9174-9180  発行年： 2018年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究において,Na_0.5Bi_0.5TiO_3-xSrTiO_3(NBT-xST,x=0,0.10,0.26)ホイスカを,テンプレートとしてNa_2Ti_6O_13ホイスカを用いて,2段階溶融塩法によって合成した。ホイスカの結晶相,形態,微細構造,組成および強誘電特性を詳細に調べた。Na_2Ti_6O_13構造からNBT-xSTペロブスカイト構造へのトポケミカル変換は,エッジ共有八面体の頂点共有八面体への構造再配列により起こることが分かった。調製した多結晶NBT-xSTホイスカは500~800nmの直径と5~10μmの長さを有する高いアスペクト比を有していた。PFM研究はNBTホイスカの好ましい圧電性を確認したが,NBT-0.26STホイスカは室温でリラクサ強誘電特性を示し,高性能マイクロ/ナノデバイスを作製するためのNBT-xSTホイスカの可能性を示した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 微細構造 ,  八面体 ,  リラクサ ,  強誘電性 ,  *融解塩 ,  *ホイスカ ,  形態 ,  アスペクト比 ,  *キャラクタリゼーション ,  多結晶
準シソーラス用語： ナノデバイス ,  圧電特性 ,  ペロブスカイト型構造 ,  結晶相 ,  *鉛フリー , 【Automatic Indexing@JST】

著者キーワード (4件)： NBT-XSTホイスカ ,  溶融塩法 ,  微細構造 ,  強誘電性

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (4件)： 鉛フリー ,  ホイスカ ,  溶融塩合成 ,  キャラクタリゼーション