サマリウム-コバルトサブミクロンファイバの合成とそれらの優れた硬磁性【JST・京大機械翻訳】

Synthesis of Samarium-Cobalt Sub-micron Fibers and Their Excellent Hard Magnetic Properties

著者 (7件)： Lee Jimin (Department of Materials Science and Chemical Engineering, Hanyang University) ,  Hwang Tae-Yeon (Department of Materials Science and Chemical Engineering, Hanyang University) ,  Kang Min Kyu (Department of Materials Science and Chemical Engineering, Hanyang University) ,  Cho Hong-Baek (Department of Materials Science and Chemical Engineering, Hanyang University) ,  Kim Jongryoul (Department of Materials Science and Chemical Engineering, Hanyang University) ,  Myung Nosang V. (Department of Chemical and Environmental Engineering, University of California, Riverside) ,  Choa Yong-Ho (Department of Materials Science and Chemical Engineering, Hanyang University)
資料名： Frontiers in Chemistry (Web)  (Frontiers in Chemistry (Web))
巻： 6  ページ： 18  発行年： 2018年 
JST資料番号： U7065A  ISSN： 2296-2646  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： スイス (CHE)  言語： 英語 (EN)

抄録/ポイント： 制御された組成と寸法を有するサマリウム-コバルトサブミクロン繊維の高スループット合成を,電気紡糸と還元-拡散プロセスを組み合わせることによって実証した。繊維の組成は前駆体組成を調整することにより容易に変化した(8<Sm<20at.%)が,繊維の直径は電気紡糸パラメータ(例えば印加電圧,溶液供給速度,温度,湿度)を変えることにより正確に制御され,単一ドメインサイズに達した。X線回折パターンにより,金属前駆体比(Sm3+/(Sm3++Co2+))が10.6%で正確に制御されたとき,単相Sm2Co17繊維が合成されたが,混合相(すなわち,Co-Sm2Co17またはSm2Co17-Sm2Co7)が化学量論から外れたときに観察された。合成繊維の磁気飽和(M_s)はSm含有量の増加と共に単調に減少した。対照的に,保磁力(H_c_i)はSm含有量の増加とともに単調に増加した。Copyright 2018 The Author(s) All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 前駆体 ,  磁気飽和 ,  永久磁石 ,  化学量論 ,  拡散過程 ,  湿度 ,  還元 ,  *サマリウム ,  合成繊維 ,  単相 ,  エレクトロスピニング ,  保磁力
準シソーラス用語： 供給速度 ,  印加電圧 ,  *硬磁性 , 【Automatic Indexing@JST】

著者キーワード (5件)： サマリウムコバルト ,  エレクトロスピニング ,  繊維 ,  永久磁石 ,  磁気的性質

分類 (2件)： 金属結晶の磁性  (BM06040T) ,  磁気的性質  (WB02020J)

タイトルに関連する用語 (2件)： サマリウム ,  硬磁性