衝撃後の機械的応答とTi-6Al-4V合金の下部組織発達に及ぼす衝撃応力振幅の影響【Powered by NICT】

Effect of shock stress amplitude on the post-shock mechanical response and substructural evolution of Ti-6Al-4V alloy

著者 (5件)： Ren Yu (School of energy, power and mechanical engineering, North China Electric Power University, Beijing 102206, PR China) ,  Xue Zhiyong (School of energy, power and mechanical engineering, North China Electric Power University, Beijing 102206, PR China) ,  luo Wenbo (School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, PR China) ,  Ren Yuejuan (School of energy, power and mechanical engineering, North China Electric Power University, Beijing 102206, PR China) ,  Zhang Yajing (School of energy, power and mechanical engineering, North China Electric Power University, Beijing 102206, PR China)
資料名： Mechanics of Materials  (Mechanics of Materials)
巻： 117  ページ： 1-8  発行年： 2018年 
JST資料番号： E0966A  ISSN： 0167-6636  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Ti-6Al-4V(Ti64)の衝撃後の機械的応答と下部組織発展に及ぼす衝撃応力振幅の影響を5.75 14.05GPaの衝撃応力範囲内で系統的に調べた。preshocked応力は14GPaを超えても衝撃後Ti64の準静的再負荷降伏挙動を室温と高温の両方で等価歪レベルで強化された衝撃誘起強化を示さなかった。衝撃後Ti64の残留による下部構造は,平面滑りが支配的である。も14.05GPaで衝撃を受けた合金中に形成されるいくつかの変形双晶。転位細胞または細胞様構造,ω相と高密度双晶のような追加強化相の欠如は,衝撃荷重によりこの合金の更なる強化を制限している。しかし,欠陥の増殖は,降伏強さの急速な増加と室温で再負荷材料の増加した歪硬化速度(SHR)をもたらした。熱軟化,降伏応力の負のSHRと低い成長率は11GPa以上の応力で衝撃を受けたTi64でより明らかな,高温で再装荷圧縮中の衝撃後の合金の動的再結晶とglobularisation上の高密度欠陥の促進によるものであった。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *衝撃 ,  衝撃波 ,  *合金 ,  降伏強さ ,  ω相 ,  歪硬化 ,  高温 ,  *下部組織 ,  動的再結晶 ,  衝撃荷重 ,  降伏応力 ,  *衝撃応力 ,  降伏 ,  変形双晶
準シソーラス用語： *応力振幅 , 【Automatic Indexing@JST】

著者キーワード (4件)： Ti-6Al-4V合金 ,  衝撃波荷重 ,  衝撃波後方の機械的応答 ,  部分構造進化

分類 (1件)： 弾性力学一般  (HC02010M)

タイトルに関連する用語 (6件)： 衝撃 ,  機械的応答 ,  Ti-6Al-4V合金 ,  下部組織 ,  発達 ,  応力振幅