Ti6Al4V上の二重PEO/BED-MOS2被覆の真空トライボロジー特性に及ぼす基板粗さの影響【JST・京大機械翻訳】

Effects of substrate roughness on the vacuum tribological properties of duplex PEO/bonded-MoS₂ coatings on Ti6Al4V

著者 (7件)： Hanjun Hu (Lanzhou Institute of Physics, China Academy of Space Technology, Lanzhou 730000, PR China) ,  Zhen Cao (Lanzhou Institute of Physics, China Academy of Space Technology, Lanzhou 730000, PR China) ,  Xingguang Liu (Lanzhou Institute of Physics, China Academy of Space Technology, Lanzhou 730000, PR China) ,  Xingguo Feng (Lanzhou Institute of Physics, China Academy of Space Technology, Lanzhou 730000, PR China) ,  Yugang Zheng (Lanzhou Institute of Physics, China Academy of Space Technology, Lanzhou 730000, PR China) ,  Kaifeng Zhang (Lanzhou Institute of Physics, China Academy of Space Technology, Lanzhou 730000, PR China) ,  Hui Zhou (Lanzhou Institute of Physics, China Academy of Space Technology, Lanzhou 730000, PR China)
資料名： Surface & Coatings Technology  (Surface & Coatings Technology)
巻： 349  ページ： 593-601  発行年： 2018年 
JST資料番号： D0205C  ISSN： 0257-8972  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,Ti-6Al-4V上のPEO/Boned-MoS_2被覆の真空トライボロジー特性に及ぼす基板粗さの影響に焦点を当てた。Ti-6Al-4V試験片の4つの異なる表面条件,すなわち,加工したままの条件において0.8,1.6,3.2,およびサンドブラストによって後処理したRa1.6を基板として用いた。ボールon 摩擦計を用いて,被覆試料の真空トライボロジー性能を評価した。結果は,Ra1.6試料が最も長い耐摩耗性寿命を示し,それは2つの原因に起因することを示した。それは,硬いPEO被覆と溝とリッジを有する特別なPEO地形である。溝はMoS_2の貯留層を提供し,リッジは硬い耐摩耗性「相」として作用した。本研究では,特別な摩耗メカニズムと粗さの影響を提案し,考察した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *トライボロジー ,  後処理 ,  耐摩耗性 ,  *被覆
準シソーラス用語： 摩耗機構 ,  サンドブラスティング ,  *トライボロジー特性 , 【Automatic Indexing@JST】

著者キーワード (4件)： 滑り摩耗 ,  プラズマ電解酸化(PEO) ,  粗さ ,  結合したMOS_2

分類 (3件)： 炭素とその化合物  (YB02060D) ,  潤滑一般  (QB02010S) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： PEO ,  MoS2 ,  真空 ,  トライボロジー特性 ,  粗さ