高速度および長寿命リチウム-硫黄電池のためのポリ硫化物変換の推進【JST・京大機械翻訳】

Propelling polysulfides transformation for high-rate and long-life lithium-sulfur batteries

著者 (12件)： Zheng Cheng (Engineering Laboratory for Functionalized Carbon Materials and Shenzhen Key Laboratory for Graphene-based Materials, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055, China) ,  Zheng Cheng (School of Materials and Energy, Guangdong University of Technology, Guangzhou 510006, China) ,  Niu Shuzhang (Engineering Laboratory for Functionalized Carbon Materials and Shenzhen Key Laboratory for Graphene-based Materials, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055, China) ,  Lv Wei (Engineering Laboratory for Functionalized Carbon Materials and Shenzhen Key Laboratory for Graphene-based Materials, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055, China) ,  Zhou Guangmin (Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Science, Shenyang 110016, China) ,  Li Jia (Engineering Laboratory for Functionalized Carbon Materials and Shenzhen Key Laboratory for Graphene-based Materials, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055, China) ,  Fan Shaoxun (Engineering Laboratory for Functionalized Carbon Materials and Shenzhen Key Laboratory for Graphene-based Materials, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055, China) ,  Deng Yaqian (Engineering Laboratory for Functionalized Carbon Materials and Shenzhen Key Laboratory for Graphene-based Materials, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055, China) ,  Pan Zhengze (Engineering Laboratory for Functionalized Carbon Materials and Shenzhen Key Laboratory for Graphene-based Materials, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055, China) ,  Li Baohua (Engineering Laboratory for Functionalized Carbon Materials and Shenzhen Key Laboratory for Graphene-based Materials, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055, China) ,  Kang Feiyu (Engineering Laboratory for Functionalized Carbon Materials and Shenzhen Key Laboratory for Graphene-based Materials, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055, China) ,  Yang Quan-Hong (Engineering Laboratory for Functionalized Carbon Materials and Shenzhen Key Laboratory for Graphene-based Materials, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055, China)
資料名： Nano Energy  (Nano Energy)
巻： 33  ページ： 306-312  発行年： 2017年 
JST資料番号： W3116A  ISSN： 2211-2855  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 均一に分布したα-Fe_2O_3ナノ粒子(Fe-PGM)と結合した三次元(3D)階層的多孔質グラフェンマクロ構造をリチウム-硫黄電池の硫黄ホストとして設計し,水熱法により調製した。このハイブリッド構造において,α-Fe_2O_3ナノ粒子は,ポリスルフィドと強く相互作用するだけでなく,より重要なことに,電荷/放電過程での不溶性化学種への変換を化学的に促進し,リチウムポリスルフィド(LiPSs)のシャトルに対する化学障壁として作用することを証明した。したがって,高速電子/イオン移動を容易にする3D階層的多孔質構造と共に,カソード中の硫黄ホストとしてのFe-PGMは,長いサイクル安定性(5Cの高電流レートで1000サイクルにわたり0.049%の超低容量フェージング速度)と共に,高レート性能(565mAhg-1)に寄与した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： ナノ粒子 ,  *電池 ,  多孔質体 ,  相互作用 ,  複合構造 ,  三次元 ,  電荷 ,  イオン輸送 ,  カソード ,  電池容量 ,  放電 ,  ポリスルフィド ,  多孔性 ,  グラフェン
準シソーラス用語： サイクル安定性 ,  シャットル ,  *リチウム硫黄電池 , 【Automatic Indexing@JST】

著者キーワード (4件)： リチウム-硫黄電池 ,  3D α-Fe_2O_3/グラフェンハイブリッド ,  酸化還元反応 ,  ポリスルフィドの変換

分類 (1件)： 二次電池  (YB04030K)

タイトルに関連する用語 (5件)： 高速度 ,  長寿命 ,  リチウム-硫黄電池 ,  ポリ硫化物 ,  推進