有限要素解析を用いた選択的レーザ融解AlSi10Mgの微細構造予測【Powered by NICT】

Microstructure prediction of selective laser melting AlSi10Mg using finite element analysis

著者 (5件)： Liu Shiwen (Wuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology, Wuhan, Hubei 430074, PR China) ,  Zhu Haihong (Wuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology, Wuhan, Hubei 430074, PR China) ,  Peng Gangyong (Wuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology, Wuhan, Hubei 430074, PR China) ,  Yin Jie (Wuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology, Wuhan, Hubei 430074, PR China) ,  Zeng Xiaoyan (Wuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology, Wuhan, Hubei 430074, PR China)
資料名： Materials & Design  (Materials & Design)
巻： 142  ページ： 319-328  発行年： 2018年 
JST資料番号： A0495B  ISSN： 0264-1275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 選択的レーザ溶融(SLM)技術は,質量と熱伝達によって制御された複雑な過程である。単線の微細構造を理解するために非常に重要である。熱変数を計算し,等軸遷移(CET)基準に柱状を用いてSLM AlSi10Mgの単線の微細構造を予測した。,溶融プール寸法とトラック表面特徴の両方によって検証した異方性熱伝導率を用いて確立した高精度過渡的三次元有限要素モデル。第二に,有限要素モデルを用いて,熱変数を正確に予測し,温度勾配,冷却速度および溶融池の凝固速度である。第三に,柱状晶から等軸晶への遷移基準を予測熱変数と実験微細構造を結合することにより確立した,実験結果は,SLM AlSi10Mgの微細構造を非常に良く予測できることを確認した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 熱伝導率 ,  *微細構造 ,  モデル ,  熱伝達 ,  温度勾配 ,  溶融池 ,  冷却速度 ,  異方性 ,  凝固速度 ,  *予測 ,  *レーザ融解 ,  柱状晶
準シソーラス用語： *有限要素 ,  FEMモデル ,  選択的レーザ溶融 ,  *有限要素解析 , 【Automatic Indexing@JST】

著者キーワード (4件)： 結晶粒構造 ,  有限要素 ,  選択的レーザ融解 ,  アディティブマニュファクチャリング

分類 (2件)： 機械的性質  (WB02030U) ,  鋳造に関する各種技術  (WC01040B)

タイトルに関連する用語 (4件)： 有限要素解析 ,  レーザ融解 ,  微細構造 ,  予測