重圧延後にアニールしたAl-0.3%CuにおけるGoss集合組織の発達【JST・京大機械翻訳】

Development of Goss texture in Al-0.3%Cu annealed after heavy rolling

著者 (6件)： Shuai L.F. (College of Materials Science and Engineering, Chongqing University, Chongqing 400045, China) ,  Huang T.L. (College of Materials Science and Engineering, Chongqing University, Chongqing 400045, China) ,  Wu G.L. (College of Materials Science and Engineering, Chongqing University, Chongqing 400045, China) ,  Huang X. (College of Materials Science and Engineering, Chongqing University, Chongqing 400045, China) ,  Huang X. (Department of Mechanical Engineering, Technical University of Denmark, 2800 Kgs. Lyngby, Denmark) ,  Mishin O.V. (Department of Mechanical Engineering, Technical University of Denmark, 2800 Kgs. Lyngby, Denmark)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 749  ページ： 399-405  発行年： 2018年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 焼鈍中のミクロ組織と集合組織の進展を,大きな初期結晶粒サイズを持つ95%冷間圧延Al-0.3%Cuの中心層で研究した。冷間圧延条件は強いBrass集合組織成分と多数のせん断帯により交差したラメラ構造から成る変形微細構造により特徴付けられる。200°Cでのアニーリング中に再結晶と析出が起こり,強いGoss集合組織が発達した。再結晶の開始において,Goss配向結晶粒は剪断帯で優先的に核形成した。再結晶の後期段階において,新しいGoss核は,支配的なBrass成分のラメラがGos配向亜粒体と相互に散在する領域に現れる。再結晶がほぼ完全であるとき,再結晶化したGos配向結晶粒は他の方位の結晶粒に成長し,それはGoss配向結晶粒の平均結晶粒サイズの急速な増加とGoss集合組織の強化をもたらす。結果として,この強く組織化された材料中のGos配向結晶粒間に新しい低角度境界が形成された。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 結晶粒 ,  *集合組織 ,  層状組織 ,  焼なまし ,  再結晶 ,  *圧延 ,  アルミニウム合金 ,  冷間圧延 ,  結晶粒径 ,  核形成 ,  高速度 ,  剪断帯 ,  微細構造

著者キーワード (5件)： アルミニウム合金 ,  冷間圧延 ,  アニーリング ,  再結晶 ,  Gossテクスチャ

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： 圧延 ,  アニール ,  Al ,  集合組織 ,  発達