バイオインプラント使用のためのRinger溶液中のホウ化物被覆チタンのフレッチング腐食応答:劣化機構の解明【JST・京大機械翻訳】

Fretting corrosion response of boride coated titanium in Ringer’s solution for bio-implant use: Elucidation of degradation mechanism

著者 (7件)： Sivakumar Bose (Indian Institute of Technology Madras, Chennai, 600036, India) ,  Sivakumar Bose (CSIR-National Metallurgical Laboratory, Jamshedpur, 831007, India) ,  Sivakumar Bose (Academy of Scientific and Innovative Research, CSIR Madras Complex, Chennai, 600113, India) ,  Pathak Lokesh Chandra (CSIR-National Metallurgical Laboratory, Jamshedpur, 831007, India) ,  Pathak Lokesh Chandra (Academy of Scientific and Innovative Research, CSIR Madras Complex, Chennai, 600113, India) ,  Singh Raghuvir (CSIR-National Metallurgical Laboratory, Jamshedpur, 831007, India) ,  Singh Raghuvir (Academy of Scientific and Innovative Research, CSIR Madras Complex, Chennai, 600113, India)
資料名： Tribology International  (Tribology International)
巻： 127  ページ： 219-230  発行年： 2018年 
JST資料番号： E0409B  ISSN： 0301-679X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ホウ化物被覆市販純チタン(CpTi)のフレッチング腐食を,開回路電位(OCP)法を用いてRinger溶液中で調べた。被覆は850,910及び1050°Cで1,3及び5時間合成した。フレッチングにより,ホウ化物試料は裸のものより低いガルバニ結合を示し,それに対応して摩耗損失を示した。TiB_2+TiBおよび/またはTiB_2厚さは,フレッチング抵抗の決定において重要な役割を果たした。不動態化/再不動態化は,それぞれホウ化物と裸のCpTiにおけるTiO_2/B_2O_3とTiO_2形成に起因する。研究は,相乗的および腐食成分の総和の抑制が被覆CpTiのフレッチング性能を改善することを明らかにした。CpTiのホウ化は生体適合性応答を強化した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *腐食 ,  摩耗 ,  *ホウ化物 ,  *被覆 ,  生体適合性 ,  *ホウ化処理 ,  電極電位 ,  不動態化 ,  *擦過腐食
準シソーラス用語： 再不動態化 ,  摩耗損失 ,  *フレッチング ,  純チタン ,  劣化機構 , 【Automatic Indexing@JST】

著者キーワード (4件)： ほう化物コーティング ,  フレッチング ,  摩耗 ,  損傷

分類 (1件)： 金属材料  (HC05020S)

タイトルに関連する用語 (6件)： インプラント ,  溶液 ,  ホウ化物 ,  チタン ,  フレッチング腐食 ,  応答