アクリルおよびエポキシ接着剤によるCFRP/アルミニウム接着接合DCB継手の疲労亀裂伝搬速度【JST・京大機械翻訳】

Fatigue crack propagation rate of CFRP/aluminum adhesively bonded DCB joints with acrylic and epoxy adhesives

著者 (5件)： Imanaka Makoto (Department of Technology Education, Osaka University of Education, Kashiwara, Osaka 582-8582, Japan) ,  Ishii Kiyoshi (Faculty of Junior College of Automobile Industry, Osaka Sangyo University, Nakagaito Daito City, Osaka 574-8530, Japan) ,  Hara Keisuke (National Institute of Technology, Yonago College, Hokona Yonago, Tottori 683-8502, Japan) ,  Ikeda Toru (Department of Mechanical Engineering, Kagoshima University, Korimoto Kagoshima, Kagoshima 890-0065, Japan) ,  Kouno Yosuke (Western Region Industrial Research Center, Hiroshima Prefectural Technology Research Institute, Agaminai Kure City, Hiroshima 737-0004, Japan)
資料名： International Journal of Adhesion and Adhesives  (International Journal of Adhesion and Adhesives)
巻： 85  ページ： 149-156  発行年： 2018年 
JST資料番号： C0153B  ISSN： 0143-7496  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 最近,構造用アクリル接着剤は,室温で硬化できるので,関心が高まっている。しかし,特に繰返し荷重下では,アクリル接着剤で接着したCFRP/金属継手の強度挙動を調べる研究はほとんどない。本研究では,アクリル接着剤で作られた接着結合CFR/アルミニウム二重片持梁(DCB)継手を用いて,疲れ亀裂成長速度を測定した。熱硬化型接着剤による疲れ亀裂成長挙動を比較するために,エポキシ接着剤を有するDCB継手について疲れ試験を行った。CFR/アルミニウム非対称継手に対して,上部被着体に対する低い被着体の厚さの比は,硬化過程で発生する残留応力により影響される亀裂先端におけるモード比と応力分布を決定する重要な因子である。アクリル及びエポキシ接着剤を用いたDCB継手の疲れ亀裂成長速度に及ぼすDCB継手の厚さ比の影響を調べた。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 非対称性 ,  疲れ試験 ,  亀裂先端 ,  残留応力 ,  疲れ亀裂成長速度 ,  応力分布 ,  *炭素繊維強化プラスチック ,  繰返し荷重 ,  疲れ亀裂成長 ,  *接着
準シソーラス用語： 被着体 ,  二重片持梁 ,  *亀裂伝搬速度 ,  *エポキシ接着剤 , 【Automatic Indexing@JST】

著者キーワード (5件)： 疲れ亀裂伝搬速度 ,  ダブルカンチレバービーム試料 ,  炭素繊維強化プラスチック ,  接着接合継手 ,  残留応力

分類 (2件)： 接合部  (HD03080V) ,  接着剤の性質・試験  (YK02000Q)

タイトルに関連する用語 (9件)： アクリル ,  エポキシ接着剤 ,  CFRP ,  アルミニウム ,  接着接合 ,  DCB ,  継手 ,  疲労 ,  亀裂伝搬速度