二段階常圧焼結により作製したMgOドープ透明結晶アルミナの機械的性質【JST・京大機械翻訳】

Mechanical Properties of MgO-Doped Transparent Crystalline Alumina Fabricated by Two-Step Pressureless Sintering

著者 (7件)： Wang Xu Dong (Shendong Coal Group Company Limited’s; Yulin, China) ,  Zhang Ya Ming (Xi’an Jiaotong University, State Key Laboratory for Mechanical Behavior of Materials; Xi’an, China) ,  Wang Zi Jing (Xi’an Jiaotong University, State Key Laboratory for Mechanical Behavior of Materials; Xi’an, China) ,  Zhi Qiang (Xi’an Jiaotong University, State Key Laboratory for Mechanical Behavior of Materials; Xi’an, China) ,  Gao Chang Le (Shendong Coal Group Company Limited’s; Yulin, China) ,  Wang Bo (Xi’an Jiaotong University, State Key Laboratory for Mechanical Behavior of Materials; Xi’an, China) ,  Yang Jian Feng (Xi’an Jiaotong University, State Key Laboratory for Mechanical Behavior of Materials; Xi’an, China)
資料名： Materials Science Forum  (Materials Science Forum)
巻： 922  ページ： 116-121  発行年： 2018年 
JST資料番号： D0716B  ISSN： 0255-5476  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： スイス (CHE)  言語： 英語 (EN)

抄録/ポイント： 高曲げ強度を有する透明多結晶アルミナを,2段階常圧焼結を用いて作製した。微細構造と機械的性質をMgOドーピング濃度と焼結パラメータを変えて調べた。結果は,粒径がMgO添加量の増加と共に著しく減少することを示した。アルミナの密度は最初の焼結段階でより高い温度により増加したが,より大きな結晶粒は曲げ強度を低下させた。したがって,最適曲げ強度は,0.5wt%MgOで,1450°C,20分間,1400°C,20hの2段階焼結で達成された。透明PCAのVickers硬度はドーピング量を増加させ,その変化傾向は相対密度により良く加速され,気孔率は結晶粒サイズよりも硬度に対してより重要であることを示した。Copyright 2018 Trans Tech Publications Ltd. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *アルミナ ,  微細構造 ,  *焼結 ,  *ドーピング ,  結晶粒 ,  パラメータ ,  空隙率 ,  曲げ強さ ,  結晶粒径 ,  相対密度 ,  硬度 ,  *酸化マグネシウム
準シソーラス用語： Vickers硬さ ,  二段階焼結 ,  *常圧焼結 , 【Automatic Indexing@JST】

著者キーワード (4件)： MgO ,  二段階焼結 ,  曲げ強さ ,  透明多結晶アルミナ

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (7件)： 段階 ,  常圧焼結 ,  作製 ,  MgO ,  ドープ ,  結晶アルミナ ,  機械的性質