表面無秩序加工CaTiO_3の増強された光触媒活性【JST・京大機械翻訳】

Enhanced photocatalytic activity of surface disorder-engineered CaTiO₃

著者 (7件)： Yan Yuxiang (State Key Laboratory of Advanced Processing and Recycling of Non-Ferrous Metals, Lanzhou University of Technology, Lanzhou 730050, China) ,  Yan Yuxiang (School of Science, Lanzhou University of Technology, Lanzhou 730050, China) ,  Yang Hua (State Key Laboratory of Advanced Processing and Recycling of Non-Ferrous Metals, Lanzhou University of Technology, Lanzhou 730050, China) ,  Yang Hua (School of Science, Lanzhou University of Technology, Lanzhou 730050, China) ,  Zhao Xinxin (School of Science, Lanzhou University of Technology, Lanzhou 730050, China) ,  Li Ruishan (School of Science, Lanzhou University of Technology, Lanzhou 730050, China) ,  Wang Xiangxian (School of Science, Lanzhou University of Technology, Lanzhou 730050, China)
資料名： Materials Research Bulletin  (Materials Research Bulletin)
巻： 105  ページ： 286-290  発行年： 2018年 
JST資料番号： B0954A  ISSN： 0025-5408  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,光触媒活性を増強する目的で,NaBH_4処理により,CaTiO_3ナノ直方体上に表面無秩序を形成することを試みた。試料をXRD,SEM,TEM,BET,XPS,UV-vis DRS,PL,EIS及び光電流応答により系統的に調べた。サンプルの光触媒活性を,模擬太陽光,UVおよび可視光の照射下でRhBを分解することによって評価した。NaBH_4処理したCaTiO_3試料は明らかに増強された光触媒活性を示した。特に,0.1MのNaBH_4溶液で処理した試料は,元のCaTiO_3より約2.0倍高い光触媒活性を有していた。これは,生成された表面無秩序が光生成電子-正孔対の分離を容易にするという事実に起因し,したがって,より多くの光生成正孔が光触媒反応に関与することができる。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 可視光 ,  電子正孔対 ,  光生成 ,  *正孔 ,  光触媒反応
準シソーラス用語： 模擬太陽 ,  電流応答 ,  *光触媒活性 , 【Automatic Indexing@JST】

著者キーワード (3件)： CaTiO_3ナノピラミッド ,  表面無秩序 ,  光触媒活性

分類 (2件)： 塩基,金属酸化物  (CD01030Z) ,  光化学反応  (CB08020F)

タイトルに関連する用語 (3件)： 無秩序 ,  増強 ,  光触媒活性