カッサバ残渣からの修飾ナノセルロース/PLA複合材料の調製と機械的性質【JST・京大機械翻訳】

Preparation and mechanical properties of modified nanocellulose/PLA composites from cassava residue

著者 (9件)： Huang Lijie (Guangxi University, Nanning 530004, China) ,  Zhang Xiaoxiao (Guangxi Key Laboratory of Clean Pulp & Papermaking and Pollution Control, Nanning 530004, China) ,  Xu Mingzi (Guangxi Key Laboratory of Clean Pulp & Papermaking and Pollution Control, Nanning 530004, China) ,  Chen Jie (Guangxi Key Laboratory of Clean Pulp & Papermaking and Pollution Control, Nanning 530004, China) ,  Shi Yinghan (Guangxi University, Nanning 530004, China) ,  Huang Chongxing (Guangxi University, Nanning 530004, China) ,  Wang Shuangfei (Guangxi University, Nanning 530004, China) ,  An Shuxiang (Qilu University of Technology, Jinan 250353, China) ,  Li Chunying (Guangxi University, Nanning 530004, China)
資料名： AIP Advances (Web)  (AIP Advances (Web))
巻： 8  号： 2  ページ： 025116-025116-7  発行年： 2018年 
JST資料番号： U7121A  ISSN： 2158-3226  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： ナノセルロースを,原料としてカッサバ残渣を,補助剤としてリン酸を用いてメカノケミカル法により調製した。調製したナノセルロースをステアリン酸で疎水的に修飾し,その分散性を改善した。この修飾ナノセルロースを,ポリ乳酸(PLA)フィルム形成液体に0%,0.5%,1.0%,1.5%,および2.0%の濃度で添加し,ポリ乳酸(PLA)フィルムの機械的性質に及ぼす改質ナノセルロースの影響を研究した。少なくとも0.5%の修飾ナノセルロースを添加すると,修飾ナノセルロースのより活性な基がPLA分子鎖上に吸着された。膜の引張強さは13.59%だけ改善されたが,膜の柔軟性は減少し,弾性係数は28.91%減少した。1%の修飾ナノセルロースを添加すると,修飾ナノセルロースとPLAは分子鎖を通して一緒に絡み合い,それらは共結晶化して安定なネットワーク構造を形成する。ナノ複合材料膜の引張強さは40.03%強化され,弾性係数は55.65%強化され,膜の柔軟性は減少した。(翻訳著者抄録)【JST・京大機械翻訳】

シソーラス用語： 柔軟性 ,  *機械的性質 ,  引張強さ ,  リン酸 ,  *カッサバ ,  分散度 ,  分子鎖 ,  ネットワーク構造 ,  複合材料 ,  弾性係数 ,  ナノ複合材料 ,  脂肪酸
準シソーラス用語： 共結晶化 ,  *ナノセルロース , 【Automatic Indexing@JST】

分類 (5件)： 食品包装  (FJ02030B) ,  高分子固体のその他の性質  (CG02025L) ,  その他の高分子の反応  (CG03040H) ,  機械的性質  (YH02022L) ,  繊維改質  (YM02050Z)

物質索引 (1件)： ステアリン酸

タイトルに関連する用語 (8件)： サバ ,  残渣 ,  修飾 ,  ナノセルロース ,  PLA ,  複合材料 ,  調製 ,  機械的性質