銀グラフェンナノ複合体を基本とする透明導電性膜のグリーン合成【Powered by NICT】

Green synthesis of silver-graphene nanocomposite-based transparent conducting film

著者 (4件)： Chamoli Pankaj (Advanced Nanoengineering Materials Laboratory, Materials Science Programme, Indian Institute of Technology Kanpur, Kanpur, India) ,  Das Malay K. (Advanced Nanoengineering Materials Laboratory, Department of Mechanical Engineering, Indian Institute of Technology Kanpur, Kanpur, India) ,  Kar Kamal K. (Advanced Nanoengineering Materials Laboratory, Materials Science Programme, Indian Institute of Technology Kanpur, Kanpur, India) ,  Kar Kamal K. (Advanced Nanoengineering Materials Laboratory, Department of Mechanical Engineering, Indian Institute of Technology Kanpur, Kanpur, India)
資料名： Physica E: Low-Dimensional Systems and Nanostructures  (Physica E: Low-Dimensional Systems and Nanostructures)
巻： 90  ページ： 76-84  発行年： 2017年 
JST資料番号： W1066A  ISSN： 1386-9477  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,銀ナノ粒子(Ag NPs)/グラフェンナノ複合材料をグリーンルートを介して簡単なソルボサーマル法によって首尾よく合成した。クエン酸は酸化グラフェン(GO)とAgイオンの還元のための環境に優しい還元剤として使用されている。硝酸銀は,Ag NPの前駆体材料として用いた。合成したままのAg NP/グラフェンナノ複合材料を,X線回折,Raman分光法,Fourier変換赤外分光法,紫外可視分光法,熱重量分析,電界放出型走査電子顕微鏡,およびX線光電子分光法によって特性化した。実験結果は,GOの還元とAg NP装飾グラフェンナノシートの形成を確認した。さらに,スプレーコーティング法は透明導電性膜の作製のために採用した。光電気特性の増強は,作製した膜の熱黒鉛化を用いて達成した。800°Cで1時間熱黒鉛は~3.4Ω/□と透過率(550nm)~66.40%のシート抵抗を用いて作製した膜の最高の性能を示し,であった。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 還元剤 ,  FTIR分光法 ,  Raman分光法 ,  X線光電子スペクトル ,  X線光電子分光法 ,  硝酸銀 ,  *ナノ複合材料 ,  *銀 ,  *透明導電膜 ,  *グラフェン ,  X線回折 ,  グラファイト ,  熱重量分析
準シソーラス用語： 電界放出型走査電子顕微鏡 ,  紫外可視分光法 ,  酸化グラフェン , 【Automatic Indexing@JST】

著者キーワード (6件)： グラフェン ,  銀 ,  ナノ複合材料 ,  還元剤 ,  シート抵抗 ,  Transmittance

分類 (1件)： 炭素とその化合物  (YB02060D)

タイトルに関連する用語 (5件)： 銀 ,  グラフェン ,  ナノ複合体 ,  透明導電性膜 ,  グリーン