パルスレーザにより誘起されたナノ双晶とZr合金におけるそれらの硬化効果【JST・京大機械翻訳】

Nanotwins induced by pulsed laser and their hardening effect in a Zr alloy

著者 (6件)： Chai Linjiang (College of Materials Science and Engineering, Chongqing University of Technology, Chongqing, 400054, China) ,  Chen Ke (College of Materials Science and Engineering, Chongqing University of Technology, Chongqing, 400054, China) ,  Zhi Yan (College of Materials Science and Engineering, Chongqing University of Technology, Chongqing, 400054, China) ,  Murty Korukonda L. (Department of Nuclear Engineering, North Carolina State University, Raleigh, NC 27695-7909, USA) ,  Chen Liang-Yu (School of Science, Jiangsu University of Science and Technology, Zhenjiang, Jiangsu 212003, China) ,  Yang Zhinan (National Engineering Research Center for Equipment and Technology of Cold Strip Rolling, Yanshan University, Qinhuangdao, 066004, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 748  ページ： 163-170  発行年： 2018年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： パルスレーザを用いて,電子チャネリングコントラストイメージング(ECC)イメージングと電子後方散乱回折(EBSD)技術によって特性化したレーザ誘起微細構造(特に緻密なナノ双晶)を有するZr-2.5Nb合金を処理した。ナノ双晶の硬化効果を,パルスレーザ処理(PLT)により改質した種々の微細構造因子からの硬度の寄与を解析することにより導出した。結果は,従来の熱機械的方法によってZr合金に導入するのが難しい緻密なナノ双晶が,50と100Wのレーザ出力でPLTによって容易に製造できることを示した。双晶系はEBSDを用いた方位解析により{10-11}〈10-12〉の圧縮型であると決定される。PLT後,試験片硬度は著しく増加し,これはNbの結晶粒微細化と固溶体だけでなく,{10-11}ナノ双晶の存在量にかなり大きく寄与し,それらの強い硬化効果を示した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 硬度 ,  キャラクタリゼーション ,  *ジルコニウム合金 ,  構造因子 ,  *パルスレーザ ,  結晶粒微細化 ,  ニオブ ,  画像処理 ,  電子チャネリング ,  レーザ出力 ,  *双晶 ,  固溶体
準シソーラス用語： Zr-2.5Nb合金 ,  EBSD ,  *ナノ双晶 , 【Automatic Indexing@JST】

著者キーワード (5件)： Zr合金 ,  パルスレーザ ,  ナノ双晶 ,  硬化 ,  電子後方散乱回折