ナノ結晶Moの押込サイズと負荷歪速度依存クリープ変形【JST・京大機械翻訳】

Indentation size and loading strain rate dependent creep deformation of nanocrystalline Mo

著者 (6件)： Zhao J. (State Key Laboratory for Strength and Vibration of Mechanical Structures, School of Aerospace, Xi’an Jiaotong University, Xi’an 710049, China) ,  Huang P. (State-Key Laboratory for Mechanical Behavior of Material, Xi’an Jiaotong University, Xi’an 710049, China) ,  Xu K.W. (State-Key Laboratory for Mechanical Behavior of Material, Xi’an Jiaotong University, Xi’an 710049, China) ,  Wang F. (State Key Laboratory for Strength and Vibration of Mechanical Structures, School of Aerospace, Xi’an Jiaotong University, Xi’an 710049, China) ,  Lu T.J. (State Key Laboratory for Strength and Vibration of Mechanical Structures, School of Aerospace, Xi’an Jiaotong University, Xi’an 710049, China) ,  Lu T.J. (MOE Key Laboratory for Multifunctional Materials and Structures, Xi’an Jiaotong University, Xi’an 710049, China)
資料名： Thin Solid Films  (Thin Solid Films)
巻： 653  ページ： 365-370  発行年： 2018年 
JST資料番号： B0899A  ISSN： 0040-6090  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ナノ結晶体心立方Mo薄膜のクリープ挙動をナノインデンテーション試験を用いて評価した。クリープ速度と対応する歪速度感受性(m)は押込みサイズと荷重歪速度(LSR)に強く依存することが分かった。面心立方金属および金属ガラスに対して以前に提案された圧子チップ-試料界面に沿った拡散の機構以外に,表面効果を含む代替機構,硬さおよびLSR依存微細構造および応力状態の逆押込サイズ効果を提案し,mの侵入深さおよびLSRの観察依存性を解釈した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 金属ガラス ,  微細構造 ,  *クリープ ,  圧子 ,  クリープ速度 ,  *ナノ結晶 ,  界面 ,  *モリブデン ,  硬度 ,  サイズ効果 ,  ナノインデンテーション ,  *歪速度 ,  FCC金属
準シソーラス用語： 歪速度感受性 ,  クリープ挙動 , 【Automatic Indexing@JST】

著者キーワード (5件)： 体中心立方 ,  貫入押込深さ ,  負荷歪速度 ,  クリープ ,  表面効果

分類 (2件)： 固体の機械的性質一般  (BL01021C) ,  金属の機械的性質  (BL01022T)

タイトルに関連する用語 (6件)： ナノ結晶 ,  Mo ,  押込 ,  サイズ ,  歪速度 ,  クリープ変形