インジウム共ドープLiNbO_3:Mo結晶の増強された光屈折特性【JST・京大機械翻訳】

Enhanced photorefractive properties of indium co-doped LiNbO₃:Mo crystals

著者 (9件)： Zhu Ling (School of Physics, Nankai University, Tianjin 300071, China) ,  Zheng Dahuai (MOE Key Laboratory of Weak-Light Nonlinear Photonics and TEDA Institute of Applied Physics, Nankai University, Tianjin 300457, China) ,  Liu Hongde (School of Physics, Nankai University, Tianjin 300071, China) ,  Saeed Shahzad (School of Physics, Nankai University, Tianjin 300071, China) ,  Wang Shuolin (School of Physics, Nankai University, Tianjin 300071, China) ,  Liu Shiguo (School of Physics, Nankai University, Tianjin 300071, China) ,  Chen Shaolin (MOE Key Laboratory of Weak-Light Nonlinear Photonics and TEDA Institute of Applied Physics, Nankai University, Tianjin 300457, China) ,  Kong Yongfa (School of Physics, Nankai University, Tianjin 300071, China) ,  Xu Jingjun (School of Physics, Nankai University, Tianjin 300071, China)
資料名： AIP Advances (Web)  (AIP Advances (Web))
巻： 8  号： 9  ページ： 095316-095316-6  発行年： 2018年 
JST資料番号： U7121A  ISSN： 2158-3226  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 種々のインジウムドーピング濃度のインジウムとモリブデンを共ドープしたニオブ酸リチウム結晶のセットを成長させ,異なる波長(442,488,532nm)での光屈折特性を調べた。1.0mol%インジウムと0.5mol%モリブデン共ドープニオブ酸リチウム結晶の回折効率は488nmで61.57%に達した。さらに,3.0mol%のインジウムおよび0.5mol%のモリブデンを共ドープしたニオブ酸リチウム結晶に対して,応答時間は,それぞれ,442nm,488nmおよび532nmにおいて0.61,0.76および0.74sに大幅に短縮され,一方,光屈折感度は,442nmにおいて7.35cm/Jに達した。これらの結果は,インジウムの共ドーピングがモリブデンをドープしたニオブ酸リチウム結晶の光屈折特性をさらに向上させる効率的な方法であることを示している。Copyright 2018 AIP Publishing LLC All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *インジウム ,  *光屈折 ,  応答時間 ,  *結晶 ,  波長 ,  ニオブ酸リチウム ,  *ドーピング ,  回折効率 ,  *モリブデン
準シソーラス用語： 共ドーピング , 【Automatic Indexing@JST】

分類 (2件)： 光物性一般  (BM08010A) ,  非線形光学  (BD05000T)

タイトルに関連する用語 (6件)： インジウム ,  ドープ ,  Mo ,  結晶 ,  増強 ,  光屈折