Fe_64Co_16Zr_10B_10非晶質合金の結晶化過程に及ぼす加熱速度の影響【Powered by NICT】

Effect of heating rates on the crystallization process of Fe₆₄Co₁₆Zr₁₀B₁₀ amorphous alloy

著者 (5件)： Yu Wanqiu (Key Laboratory of Functional Materials Physics and Chemistry of the Ministry of Education, Jilin Normal University, Siping 136000, Jilin, PR China) ,  Zeng Haoqun (Key Laboratory of Functional Materials Physics and Chemistry of the Ministry of Education, Jilin Normal University, Siping 136000, Jilin, PR China) ,  Sun Yaming (Key Laboratory of Functional Materials Physics and Chemistry of the Ministry of Education, Jilin Normal University, Siping 136000, Jilin, PR China) ,  Sun Yajuan (Tianjin Polytechnic University, Tianjin 300387, PR China) ,  Hua Zhong (Key Laboratory of Functional Materials Physics and Chemistry of the Ministry of Education, Jilin Normal University, Siping 136000, Jilin, PR China)
資料名： Physics Letters. A  (Physics Letters. A)
巻： 381  号： 18  ページ： 1573-1576  発行年： 2017年 
JST資料番号： C0600B  ISSN： 0375-9601  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 単ロール溶融紡糸法によって作成したFe_64Co_16Zr_10B_10非晶質合金を種々の加熱速度下で1時間の550と600と650と750°Cでアニールした。合金の熱的性質,微細構造と磁気特性を同時熱分析(STA),X線回折(XRD),透過型電子顕微鏡(TEM)および振動試料磁力計(VSM)により調べた。同じ加熱温度では,非晶質合金の結晶化は加熱速度の変化と共に異なっていた。加熱速度と微細構造の関係を検討した。加熱速度は元素の分布に影響し,結晶化生成物の違いをもたらした。初期結晶化段階でFe_64Co_16Zr_10B_10合金の保磁力(H c)は加熱速度の減少により改善できる。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *結晶化 ,  溶融紡糸 ,  熱分析 ,  透過型電子顕微鏡 ,  微細構造 ,  *非晶質合金 ,  熱特性 ,  *加熱速度 ,  磁気的性質 ,  加熱温度 ,  *合金 ,  X線回折 ,  保磁力