熱変形ナノ結晶SmCo_5磁石における結晶集合組織形成に及ぼす相組成の影響【JST・京大機械翻訳】

Effect of phase composition on crystal texture formation in hot deformed nanocrystalline SmCo₅ magnets

著者 (7件)： Ma Qiang (College of Materials Science and Engineering, Beijing University of Technology, Beijing, China) ,  Yue Ming (College of Materials Science and Engineering, Beijing University of Technology, Beijing, China) ,  Xu Xiaochang (College of Materials Science and Engineering, Beijing University of Technology, Beijing, China) ,  Zhang Hongguo (College of Materials Science and Engineering, Beijing University of Technology, Beijing, China) ,  Zhang Dongtao (College of Materials Science and Engineering, Beijing University of Technology, Beijing, China) ,  Zhang Xuefeng (Key Laboratory of Integrated Exploitation of Bayan Obo Multi-Metal Resources, Inner Mongolia University of Science and Technology, Baotou, China) ,  Zhang Jiuxing (College of Materials Science and Engineering, Beijing University of Technology, Beijing, China)
資料名： AIP Advances (Web)  (AIP Advances (Web))
巻： 8  号： 5  ページ： 056214-056214-4  発行年： 2018年 
JST資料番号： U7121A  ISSN： 2158-3226  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本研究では,バルク異方性ナノ結晶SmCo_5磁石をホットプレスとそれに続く熱間変形法により調製した。集合組織と磁気特性に及ぼす相組成の影響を提示し,それに基づいて,熱間変形過程の間の塑性変形と集合組織形成の機構を議論した。SmCo_5磁石を熱間変形によって調製し,2.5wt%と10wt%の過剰SmをSm蒸発による重量損失を補償するために添加した。著者らの解析は,相組成がSmCo_5磁石の集合組織を決定する最も重要なパラメータの1つであることを明らかにした。したがって,2:17相の存在とその相変態が,ナノ結晶SmCo_5磁石の磁気特性と同様に,結晶集合組織形成を強調することが示唆された。(翻訳著者抄録)【JST・京大機械翻訳】