タングステンにおけるインデンテーションサイズ効果:HR-EBSDを用いた圧痕の下での幾何学的に必要な転位の定量化【JST・京大機械翻訳】

Indentation size effect in tungsten: Quantification of geometrically necessary dislocations underneath the indentations using HR-EBSD

著者 (4件)： Javaid Farhan (Physical Metallurgy Division, Materials Science Department, Technische Universitaet Darmstadt, Alarich-Weiss-Strasse 2, 64287 Darmstadt, Germany) ,  Xu Yukun (Physical Metallurgy Division, Materials Science Department, Technische Universitaet Darmstadt, Alarich-Weiss-Strasse 2, 64287 Darmstadt, Germany) ,  Bruder Enrico (Physical Metallurgy Division, Materials Science Department, Technische Universitaet Darmstadt, Alarich-Weiss-Strasse 2, 64287 Darmstadt, Germany) ,  Durst Karsten (Physical Metallurgy Division, Materials Science Department, Technische Universitaet Darmstadt, Alarich-Weiss-Strasse 2, 64287 Darmstadt, Germany)
資料名： Materials Characterization  (Materials Characterization)
巻： 142  ページ： 39-42  発行年： 2018年 
JST資料番号： D0448C  ISSN： 1044-5803  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 低欠陥密度結晶材料の押込み試験の間に,より高い硬度値がより低い押込深さで見出され,それは押込みサイズ効果と呼ばれる。硬さの深さ依存性はNix-Gaoモデルによって記述できる。それは幾何学的に必要な転位(GNDs)の概念に基づいている。しかし,基礎となる転位機構は残っているが,押込下でのGND密度の独立した測定が必要である。本研究では,GND密度の深さ依存性を高分解能電子後方散乱回折によりタングステン中のBerkovich圧痕の下で定量化した。より高いGND密度がより低い押込深さに対して見出され,測定したGND密度に対してより高いTaylor硬度をもたらした。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *幾何学 ,  *サイズ効果 ,  結晶 ,  *タングステン ,  硬度 ,  高分解能 ,  *圧痕 ,  欠陥密度
準シソーラス用語： *EBSD ,  押込試験 ,  深さ依存性 ,  押込み深さ , 【Automatic Indexing@JST】

著者キーワード (5件)： タングステン ,  押込サイズ効果 ,  幾何的に必要な転位 ,  HR-EBSD ,  ECCI

分類 (3件)： 金属の機械的性質  (BL01022T) ,  変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (8件)： タングステン ,  インデンテーション ,  サイズ効果 ,  EBSD ,  圧痕 ,  幾何学 ,  転位 ,  定量化