Zr55Cu30Al10Ni5バルク金属ガラスの破壊靱性に及ぼす鋳放し球晶の影響【JST・京大機械翻訳】

Influence of as-cast spherulites on the fracture toughness of a Zr55Cu30Al10Ni5 bulk metallic glass

著者 (6件)： Hin S. (Univ. Bretagne Sud, UMR CNRS 6027, IRDL, F-56321 Lorient, France) ,  Bernard C. (Univ. Bretagne Sud, UMR CNRS 6027, IRDL, F-56321 Lorient, France) ,  Doquet V. (Laboratoire de Mecanique des Solides, Ecole Polytechnique, UMR CNRS 7649, Univ. Paris Saclay Palaiseau, France) ,  Yokoyama Y. (Laboratory for Advanced Materials, Institute for Materials Research, Tohoku University, Katahira 2-1-1 Aoba-ku Sendai City, Miyagi Prefecture 980-8577, Japan) ,  Magueresse A. (Univ. Bretagne Sud, UMR CNRS 6027, IRDL, F-56321 Lorient, France) ,  Keryvin V. (Univ. Bretagne Sud, UMR CNRS 6027, IRDL, F-56321 Lorient, France)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 740-741  ページ： 137-147  発行年： 2019年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,その破壊挙動に及ぼす加工条件によるバルク金属ガラスのガラス状マトリックス中に存在する可能性のある鋳放し球晶の影響を検討した。低分率鋳造球晶(~1%体積分率)を含むZr55Cu30Al10Ni5ガラスの破壊靭性を曲げ試験により調べた。得られたモード1破壊靭性値は約72MPamであり,球晶の中程度の有害効果を明らかにした。この結果を,文献からの結果と同様に,同じ組成のフラウレスおよびデンドライト含有ガラスに対する以前の結果と比較した。モードIおよびIIの下での亀裂伝搬における球晶による役割プライド,および破壊を破面観察および有限要素計算によって最終的に検討した。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 体積率 ,  亀裂伝搬 ,  モード1 ,  亀裂 ,  *球晶 ,  *ガラス ,  曲げ試験 ,  鋳造 ,  樹枝状結晶 ,  *鋳放し ,  *バルク金属ガラス ,  *靱性 ,  加工条件 ,  *破壊靱性
準シソーラス用語： 破面観察 , 【Automatic Indexing@JST】

著者キーワード (6件)： 亀裂 ,  破壊 ,  金属ガラス ,  靭性 ,  加工 ,  結晶欠陥

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： バルク金属ガラス ,  破壊靱性 ,  鋳放し ,  球晶