マルエージング350鋼:回折,磁気および超微細解析による老化を追跡【Powered by NICT】

Maraging-350 steel: Following the aging through diffractometric, magnetic and hyperfine analysis

著者 (6件)： Nunes G.C.S. (Universidade Estadual de Maringa, Departamento de Fisica, Av. Colombo, 5790, PR, 87.020-900 Brazil) ,  Sarvezuk P.W.C. (Universidade Tecnologica Federal do Parana, Campo Mourao, PR, Brazil) ,  Alves T.J.B. (Universidade Estadual de Maringa, Departamento de Fisica, Av. Colombo, 5790, PR, 87.020-900 Brazil) ,  Biondo V. (Universidade Estadual de Maringa, Departamento de Fisica, Av. Colombo, 5790, PR, 87.020-900 Brazil) ,  Ivashita F.F. (Universidade Estadual de Maringa, Departamento de Fisica, Av. Colombo, 5790, PR, 87.020-900 Brazil) ,  Paesano A. (Universidade Estadual de Maringa, Departamento de Fisica, Av. Colombo, 5790, PR, 87.020-900 Brazil)
資料名： Journal of Magnetism and Magnetic Materials  (Journal of Magnetism and Magnetic Materials)
巻： 421  ページ： 457-461  発行年： 2017年 
JST資料番号： H0644A  ISSN： 0304-8853  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 溶体化焼なましマルエージング350鋼の板を不活性雰囲気下での経時変化を受けさせ,時間及び温度を変化させた。時効した試料をX線回折とMoessbauer分光法によって特性化した。結果は時効処理は,オーステナイトの復帰を誘導し,時間と熱処理の温度と共に変化する量であることを明らかにした。超微細パラメータと同様に,マルテンサイト相とオーステナイト相の格子パラメータは,全てのエージング条件で得られた。金属間化合物は熟成した試料のいずれにおいても同定されなかったが,貧弱に結晶化した相分率,不完全なマルテンサイト→オーステナイト逆変態の結果,いくつかの試料で観察された。溶体化焼なまし鋼におけるマルテンサイトにより提示された立方対称性から正方晶歪は時効後に除去されなかった。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 結晶化 ,  金属間化合物 ,  経時変化 ,  オーステナイト ,  焼なまし ,  時効 ,  マルテンサイト ,  逆変態 ,  X線回折 ,  格子定数 ,  Moessbauer分光法 ,  正方晶系 ,  対称性 ,  溶体化処理 ,  *鋼

著者キーワード (6件)： マルエージング350鋼 ,  マルテンサイト ,  加齢 ,  オーステナイト ,  Rietveld精密化 ,  メスバウアー分光