ベータ変態以下でのジルカロイ-4の変形誘起相変態【Powered by NICT】

Deformation-induced phase transformation in Zircaloy-4 below the beta transus

著者 (8件)： Aranas Clodualdo (Materials Engineering, McGill University, 3610 University St., Montreal H3A 0C5, Canada) ,  Aranas Clodualdo (CanmetMATERIALS, Natural Resources Canada, 183 Longwood Road South, Hamilton, Ontario L8P 0A1, Canada) ,  Guo Baoqi (Materials Engineering, McGill University, 3610 University St., Montreal H3A 0C5, Canada) ,  Rodrigues Samuel (Materials Engineering, McGill University, 3610 University St., Montreal H3A 0C5, Canada) ,  Choi Joonphil (Materials Engineering, McGill University, 3610 University St., Montreal H3A 0C5, Canada) ,  Kim Sanghoon (Korea Institute of Materials Science, Powder Technology Department, Changwon 51508, South Korea) ,  Sun Binhan (Materials Engineering, McGill University, 3610 University St., Montreal H3A 0C5, Canada) ,  Jonas John J. (Materials Engineering, McGill University, 3610 University St., Montreal H3A 0C5, Canada)
資料名： Materials Letters  (Materials Letters)
巻： 220  ページ： 229-233  発行年： 2018年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 動的変態はβトランザス以上及び以下の温度における鋼とチタン合金の起こることを示した。硬質相は変形中に軟質相に変態する。この異常な冶金学的現象は以前に変換軟化(Ghoshetal.,2016)の観点から説明した。本研究では,圧縮試験をβトランザス以下の温度でのジルカロイ-4の試料で行った。微細構造と微小硬さ測定をαは温度での変形中に変位型を形質転換するベータに変態点以下約75°Cに低下することを示した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 微細構造 ,  転移温度 ,  微小硬さ ,  鋼 ,  *ジルカロイ ,  圧縮試験 ,  チタン合金
準シソーラス用語： 軟質 ,  *ジルカロイ4 , 【Automatic Indexing@JST】

著者キーワード (3件)： 動的変換 ,  ジルカロイ-4 ,  ベータZr

分類 (1件)： 半導体結晶の電気伝導  (BM03043X)

タイトルに関連する用語 (4件)： 変態 ,  ジルカロイ-4 ,  誘起 ,  相変態