Pb-0.09%Ca-1.23%Sn合金の硬さと電気化学的挙動に及ぼす凝固後の急冷の影響【JST・京大機械翻訳】

Effect of quenching after solidification on hardness and electrochemical behavior of a Pb-0.09%Ca-1.23%Sn alloy

著者 (6件)： Seyedi M. (Materials and Metallurgical Engineering Department, Ferdowsi University of Mashhad, Mashhad 91775-1111 Iran) ,  Kosari A. (Materials and Metallurgical Engineering Department, Ferdowsi University of Mashhad, Mashhad 91775-1111 Iran) ,  Nakhaie D. (Materials and Metallurgical Engineering Department, Ferdowsi University of Mashhad, Mashhad 91775-1111 Iran) ,  Moayed M.H. (Materials and Metallurgical Engineering Department, Ferdowsi University of Mashhad, Mashhad 91775-1111 Iran) ,  Alagheband A. (Department of Chemical Engineering, Faculty of Engineering, Islamic Azad University, Quchan, Iran) ,  Azimi M.Y. (Chemical Engineering Department, Ferdowsi University of Mashhad, Mashhad 91775-1111, Iran)
資料名： Journal of Energy Storage  (Journal of Energy Storage)
巻： 17  ページ： 441-445  発行年： 2018年 
JST資料番号： W3042A  ISSN： 2352-152X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,統計的アプローチにより,Pb-0.09%Ca-1.23%Sn正格子合金の硬化性と初期電気化学的性質に及ぼす焼入れ法としての水噴霧プロセスの影響を研究した。ノズル直径,焼入れ温度及び時効時間は合金硬度に影響を及ぼすと考えられるが,二つの第一因子は電気化学的挙動を説明すると信じられている。応答曲面法(RSM)を用いて実験を設計し,データを解析した。その結果,焼入れ試料は初期時効時間で許容できる硬度を獲得し,その硬度は室温での4日時効後の空冷試料よりも高いことを示した。データを統計的に解析することにより,時効時間が硬度を増加させるが,研究した範囲の水温度とノズル直径はかなりの影響を持たないことが分かった。加えて,PbSO_4/PbO_2の著しい変化と合金の酸素発生ポテンシャルは水噴霧で観察されないが,不動態電流密度の減少は水温低下の結果として顕著である。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 空気冷却 ,  焼入 ,  *凝固 ,  電流密度 ,  応答曲面法 ,  *スズ合金 ,  *合金 ,  噴霧法 ,  時効 ,  *電気化学的挙動 ,  *硬度 ,  水温 ,  不動態
準シソーラス用語： 水噴霧 ,  電気化学的特性 , 【Automatic Indexing@JST】

著者キーワード (5件)： Pb-Ca-Sn合金 ,  焼入 ,  硬化 ,  電気化学的挙動 ,  応答曲面法