アルミナ-スピネルキャスタブルの性質に及ぼす反応性アルミナの粉末特性の影響【JST・京大機械翻訳】

Influence of powder characteristics of reactive alumina on properties of alumina-spinel castables

著者 (7件)： Zhang Danyang (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, China) ,  Li Chunxue (Imerys Technical Center China, Tianjin, China) ,  Jiang Nian (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, China) ,  Gao Jianying (Imerys Technical Center China, Tianjin, China) ,  Touzo Bruno (Imerys Technical Center China, Tianjin, China) ,  Yuan Wenjie (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, China) ,  Yuan Wenjie (National-provincial Joint Engineering Research Center of High Temperature Materials and Lining Technology, Wuhan University of Science and Technology, Wuhan, China)
資料名： Ceramics International  (Ceramics International)
巻： 44  号： 8  ページ： 9984-9990  発行年： 2018年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： アルミナ-スピネルキャスタブルは,高温産業において広範囲の応用がある。種々の反応性アルミナ添加の異なる粉末特性の影響を調べるために,異なる温度(1500°Cと1650°C)で焼成したアルミナ-スピネルキャスタブルの特性を調べた。異なるキャスタブルのマトリックスのレオロジー挙動を比較した。最大比表面積と活性を有する反応性アルミナ(A)を含むマトリックスのスラリーは,高せん断速度で最低粘度を有することを実証した。これはキャスタブルの成形に有益であった。微細な反応性アルミナ粉末に対して,キャスタブルの膨張と気孔率の差は鉱物学的および微細構造的進化に起因し,それは粒子サイズとNa_2O不純物レベルによって影響された。ヘキサアルミン酸カルシウム(CA_6)とCM_2A_8の形成は,キャスタブルの強度を強化することにおいて重要な役割を果たした。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *粉体 ,  剪断速度 ,  空隙率 ,  アルミン酸カルシウム ,  レオロジー ,  *スピネル ,  *アルミナ ,  比表面積 ,  スラリー ,  粒度 ,  *反応性 ,  高温 ,  微細構造 ,  不純物
準シソーラス用語： 低粘度 , 【Automatic Indexing@JST】

著者キーワード (5件)： コランダム ,  スピネル ,  キャスタブル ,  レオロジー ,  特性

分類 (1件)： 耐火物  (YC04030N)

タイトルに関連する用語 (4件)： アルミナ ,  性質 ,  反応性 ,  粉末