150°Cで修飾されたS690鋼材の破壊靭性に及ぼすノッチの鈍さの効果【Powered by NICT】

Notch bluntness effects on fracture toughness of a modified S690 steel at 150°C

著者 (6件)： Kim J.-S. (Department of Mechanical Engineering, Korea University, Anam-Dong, Seongbuk-Gu, Seoul 136-701, South Korea) ,  Larrosa N.O. (Department of Mechanical Engineering, University of Bristol, Queen’s Building, University Walk, Bristol BS8 1TR, UK) ,  Larrosa N.O. (School of Mechanical, Aerospace & Civil Engineering, The University of Manchester, Manchester M13 9PL, UK) ,  Horn A.J. (Clean Energy Europe - Nuclear Services, Amec Foster Wheeler, Warrington WA3 6XF, UK) ,  Kim Y.-J. (Department of Mechanical Engineering, Korea University, Anam-Dong, Seongbuk-Gu, Seoul 136-701, South Korea) ,  Ainsworth R.A. (School of Mechanical, Aerospace & Civil Engineering, The University of Manchester, Manchester M13 9PL, UK)
資料名： Engineering Fracture Mechanics  (Engineering Fracture Mechanics)
巻： 188  ページ： 250-267  発行年： 2018年 
JST資料番号： A0119A  ISSN： 0013-7944  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本論文では,鋼の構造健全性評価に鈍的欠陥の影響を検討した。種々の切欠き視力と平滑引張,切欠き棒の引張と多重試験片単一端部切欠き曲げ試験を行い,増加切欠き半径を用いた効果的な延性破壊靭性の増加を示した。延性破壊モデルは厚さ方向延性き裂伸展の局所変動を含む試験片応答を予測できることが示されている。へき開破壊靭性に及ぼす切欠き半径の影響を記述するために開発された経験的適合を調べ,また延性破壊靭性に及ぼす切欠き半径の影響を記述できることが分かった。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 延性破壊 ,  引張 ,  亀裂伝搬 ,  延性 ,  多重化 ,  *切欠き ,  曲げ試験 ,  *鋼 ,  *破壊靱性 ,  *鋼材
準シソーラス用語： 構造健全性 , 【Automatic Indexing@JST】

著者キーワード (5件)： 低下させる切欠き ,  破壊評価図 ,  欠陥評価 ,  延性破壊モデル ,  有効破壊靭性